Supercapacitor based on polymeric binary composite of polythiophene and single

Scientific Reports volume 12, Article number: 11278 (2022) Cite this article

1903 Accesses

9 Citations

Metrics details

The aim of this work is to fabricate supercapacitor electrode based on poly (3-hexyl-thiophene-2, 5-diyl) (P3HT) and single-walled carbon nanotubes (SWCNTs) nanocomposites with different ratios onto a graphite sheet as a substrate with a wide voltage window in nonaqueous electrolyte. Structural, morphological and electrochemical properties of the prepared nanocomposites of P3HT/SWCNTs were studied and discussed. The electrochemical properties included cyclic voltammetry (CV), galvanostatic charging-discharging (GCD), and electrochemical impedance spectroscopy (EIS) were investigated. The obtained results indicated that P3HT/SWCNTs nanocomposite possesses higher specific capacitance than that present in its individual component. The high electrochemical performance of the nanocomposite was due to formation of microporous structure which facilitates ions diffusion and electrolyte penetration in these pores. The morphological micrographs of the purified SWCNTs had buckypaper structure while the photomicrographs of P3HT/SWCNTs showed that SWCNTs appear behind and front of the P3HT nanospheres. The specific capacitance of 50% SWCNTs at 0.5 Ag−1 was found to be 245.8 Fg−1 compared with that of pure P3HT of 160.5 Fg−1.

Since the discovery of the conducting polymers like poly (3‐hexylthiophene) (P3HT), polypyrrole and polyaniline, many scientists have been working on finding applications for these polymers as light emitting diodes1,2, adsorbents3,4, electrochromic devices5, sensors6, and supercapacitors7,8. Electrochemical supercapacitors as promising energy storage devices provide low energy density, high power density, fast charging discharging rate and long cycle lifetime9,10. Supercapacitors (SC) or ultracapacitors have pointed out to capacitors with high-surface area of the electrodes. SCs can harvest energy in very short time to provide spurt of energy when a quick charge is required. Based on charge and discharge mechanism, supercapacitors are categorized into electric double-layer supercapacitors (EDLCs), pseudosupercapacitors (PSC) and hybrid supercapacitors. EDLCs are also called electrostatic capacitors and the charge storage in EDLCs takes place at the electrode/electrolyte interface through the electrostatic charge adsorption mechanism11,12. The specific capacitance of this type relies on the specific surface area, pore size, pore shape, morphology and electrical conductivity. In PSCs store charges via fast and reversible redox or Faradic reactions occurring on metal oxides or conducting polymers. The reversible redox reactions occurred at the surface of the electrode materials produce high energy density compared to EDLCs10,13,14.

Among PSC materials, conductive polymers and transition metal oxides are promising materials as SC electrodes. P3HT, polypyrrole and polyaniline are interested in the field of energy storage due to their electrochemical reversibility, doping–dedoping during the charge–discharge process, and high electrical conductivity9,15. P3HT as a soluble conducting polymer is suitable and appropriate for the fabrication of supercapacitor electrode because of its pseudosupercapacitance behavior, unique electrical conductivity and high energy density16. In addition, P3HT combined with carbon nanostructures can store the charge at electrical double layer formed at electrode/electrolyte interface. However, swelling and shrinkage of the P3HT in the electrolytes lead to mechanical degradation17,18,19.

Single-wall carbon nanotubes (SWCNTs) and multi-walled carbon nanotubes (MWCNTs) have used as electrodes for the supercapacitors due to their unique hollow structure, electronic conductivity, thermal stability and mechanical strength20,21. Many efforts have been made to fabricate P3HT/SWCNTs electrode because of their high specific surface area, which can expose entirely either basal graphite planes or edge planes to the electrolyte22,23,24,25. Dhibar et al. prepared graphene/SWCNTs/poly(3-methylthiophene) ternary nanocomposite supercapacitor electrodes and achieved a specific capacitance of 551 F/g with a small voltage window between 0 and 0.8 V23. Zhou et al. grafted and fabricated poly(3-oligo(ethylene oxide)) thiophene onto SWCNTs supercapacitor electrode in the negative window from − 0.9 to − 0.1 V and obtained a specific capacitance of 399 F/g25.

Herein, we report specific capacitances of 245 Fg−1 at 0.5 Ag−1 for the fabricated supercapacitor electrode with a wide voltage window based on P3HT/SWCNTs nanocomposite electrode onto a graphite sheet as a substrate in 0.1 M LiClO4. P3HT/SWCNTs nanocomposites with different ratios by physical blend were prepared. The electrochemical properties of these electrodes were investigated via CV, GCD, and EIS measurements. The obtained results indicated that P3HT/SWCNTs nanocomposite electrodes possess higher specific capacitance than the pristine component. The good electrochemical performance of the nanocomposite is attributed to π–π interactions between SWCNTs and P3HT and formation of microporous structure to facilitate rapid ions diffusion and electrolyte penetration in these pores.

In order to investigate the changes in the chemical structures of P3HT, SWCNTs and P3HT/SWCNTs nanocomposites with different SWCNTs ratios, infrared and Raman spectra are analyzed as described as follow. Figure 1 illustrates the absorption peaks of the infrared spectra of P3HT and P3HT/10% SWCNTs, P3HT/25% SWCNTs and P3HT/50% SWCNTs nanocomposites. The absorption peak at 3448 cm−1 belongs to the O–H stretching vibration. The small peak at ~ 3051 cm−1 is ascribed to the C–H aromatic stretching vibration of the thienyl ring. The features in 2922–2855 cm−1 range correspond to the –CH3 and –CH2– stretching vibrations of the hexyl side chains26,27,28. Characteristic band at 1509 cm−1 is corresponded to C = C vibration of quinoid unit of the polymer chain. In addition, the band at 1452 cm−1 is ascribed to the C–C ring stretching. Moreover, C–H and C–O–C stretching vibrations appear at 1310 and 1175 cm−1, respectively. The weak bands at 878 and 825 cm−1 are assigned to the C–H out-of-plane stretching and bending vibrations of the thiophene ring, respectively. The small band at 670 cm−1 is due to C–S bending of P3HT. FTIR spectra of P3HT/SWCNTs nanocomposites with different ratios of SWCNTs have the same features of pristine P3HT without shifting. This indicates that the P3HT/SWCNTs nanocomposites are formed because of the simple π–π stacking interactions instead of other stronger interactions between P3HT and SWCNTs29.

FTIR spectra of P3HT, and P3HT/50% SWCNTs, P3HT/25% SWCNTs and P3HT/10% SWCNTs nanocomposites.

Raman spectroscopy is conducted to investigate the structural configurations of the carbon-based materials. Figure 2 displays the Raman bands of SWCNTs, P3HT, and P3HT/SWCNTs nanocomposites with different SWCNTs ratios. As illustrated in Fig. 2a, the pristine SWCNTs shows that Raman spectrum exhibits the radial breathing modes (RBMs) with two peaks at 264 and 158.8 cm−1, a sharp order G band at 1586 cm−1, a weak disorder D band at 1342 cm−1, and a small 2D band at 2671 cm−125. Raman spectra of the pure P3HT and P3HT/SWCNTs nanocomposites with different ratios are depicted in Fig. 2b and compared with the pristine SWCNTs bands. Firstly, the pure P3HT shows main dominant peaks at around 1444 and 1375 cm−1 corresponding to the characteristic C=C and C–C in-phase vibrations of the thiophene rings, respectively25. There are also two small bands observed at 2895 and 1091 cm−1 assigned to the C–H stretching and bending, respectively. In addition, a small peak at 1207 cm−1 is attributed to C–C stretching and the band at 725 cm−1 is corresponded to C–S–C ring deformation30.

Raman spectra of (a) pristine SWCNTs, (b) P3HT/SWCNTs nanocomposites with different ratios of SWCNTs, (c) analysis of the D, G and 2D band, Inset of (c) presents the ID/IG ratios and (d) analysis of the RBMs band.

Notably, the P3HT/SWCNTs nanocomposites spectra exhibit the characteristic peaks of the pure P3HT as well as the G, D and 2D bands of SWCNTs, respectively. Figure 2c presents the D, G, and 2D bands in the Raman spectra of the pristine SWCNTs and PHT/SWCNTs nanocomposites. The sharp order G band is associated with the sp2 hybridized carbon atoms in the nanotubes wall and the weak disorder D band is sensitive to the sidewall sp3 hybridized carbon atoms created by covalent functionalization (i.e., indicates the existence of structural defects on the surfaces of SWCNTs)24. The resonant 2D band is considered as an overtone of the D band. The surface modifications and the functionalization degree on the nanotube walls can be evaluated via the ID/IG ratio. The high intensity values of this ratio enhance the surface functionalization on the nanotube walls31,32. As shown in the inset of Fig. 2c, the ID/IG ratios are calculated for both the pristine SWCNTs and the P3HT/SWCNTs nanocomposites with different SWCNTs ratios. For P3HT/SWCNTs nanocomposites, ID/IG ratio is increased as ratio of the SWCNTs increases and P3HT is anchored on the surface of the SWCNTs. It is noted that 50% SWCNTs nanocomposite exhibits the highest homogenous mixing between the P3HT and SWCNTs. G band position can be used to evaluate the charge transfer in SWCNTs composites33,34,35. The redshift is a result of the charge transfer from the electron donors in P3HT to the π-system of the SWCNTs33,34,35. Thus, the redshift of the G band in the P3HT/SWCNTs nanocomposites is due to π-π stacking interaction between P3HT and SWCNTs. Hence, it is clearly visible that the 50% SWCNTs nanocomposite has the highest redshift value and thus has the better charge transfer interaction and facilitates the ions diffusion of the electrolyte.

The analysis of the RBMs of the pristine SWCNTs and P3HT/SWCNTs nanocomposites with different SWCNTs ratios is depicted in Fig. 2d. The RBMs are corresponded to the coherent vibration of the carbon atoms in the radial direction of the nanotubes (i.e., as if the nanotubes are "breathing")35. The RBMs of SWCNTs are used to estimate their diameters (d) via the positions of the Raman peaks (ωRBM) using c/ωRBM36 (where the constant c is 248.3 nm/cm−137. It is observed that there are two diameters for the pristine SWCNTs with 0.94 and 1.56 nm. On the other hand, the P3HT/SWCNTs nanocomposites exhibit RBMs with only one peak, which is shifted to different peak position. The presence of the RBMs in the nanocomposites spectra confirms the embedded of the SWCNTs in the composite. The appearance of this peak in the nanocomposite leads to the translation of the SWCNTs to a dominate mean diameter38. Hence, the estimated mean diameters for the 10, 25, and 50% SWCNTs nanocomposites are 1.2, 1.26, 1.21 nm, respectively. It is noticed that the small-diameter SWCNTs in the composite are apparently eradicated expected for the 25% SWCNTs sample and the presence of the peak with the blue asterisk is attributed to the unreacted SWCNTs in the composite.

Figure 3 illustrates the scanning electron micrographs of SWCNTs, pure P3HT and P3HT/SWCNTs nanocomposites at different SWCNTs contents. The SEM micrographs of the purified SWCNTs sample at different magnifications shown in Fig. 3a have a paper-like morphology or buckypaper structure. This structure is the product of the filtration step during the purification process of SWCNTs synthesis. After the filtration step, SWCNTs are closer to each other to form rigid bundles. These bundles are hard to see by SEM at high magnifications. However, as shown in Fig. 3a some bundles are observed at the boundaries, which serve as a connection between the sheets of the buckypaper39.

SEM images of: (a) purified SWCNTs, (b) pure P3HT, (c) P3HT/10% SWCNTs, (d) P3HT/25% SWCNTs and (e) P3HT/50% SWCNTs. The inset images are the samples at high magnification.

The pure P3HT shows randomly and dispersed microgranulars and small particles structure as presented in Fig. 3b. The size of microgranulars is about 0.5 μm. The SEM images in Fig. 3c–e illustrate the photomicrographs of P3HT/10% SWCNTs, P3HT/25% SWCNTs and P3HT/50% SWCNTs, respectively. P3HT/10% SWCNTs nanocomposite image displays a compact and homogenous layer due to the dominant component of P3HT as shown in Fig. 3c. On the other hand, at high percentages of SWCNTs of 25 and 50% there are different phases in the formed nanocomposites. There are large numbers of voids and polythiophene particles or granules shielded and masked the SWCNTs as displayed in Fig. 3d. Generally, there are tubular and some globular structures for P3HT/SWCNTs nanocomposites. As the percentage of SWCNTs in P3HT/SWCNTs increases, the tubular structure is observed indicating that SWCNTs act as hard templates onto P3TH deposited to form the tubular morphology40.

HR-TEM is carried out to investigate the interior features of purified SWCNTs, pure P3HT and P3HT/50% SWCNTs nanocomposite as shown in Fig. 4. Figure 4a illustrates TEM image of SWCNTs with a large quantity of bundles with a diameter less than 25 nm (inset of Fig. 4a). The bundles of these nanotubes are relative clean, smooth surface and a coil-like structure. Figure 4b presents TEM image of pristine P3HT with typical nanosheets or spherical structure. These sheets are coagulated and aggregated together with small particles and granules. The P3HT/50% SWCNTs nanocomposite images have a phase separation of their two components (nanotubes and nanosheets nanospheres) and in some regions the nanotubes appear behind and front of the P3HT spheres as illustrated in HR-TEM images shown in Fig. 4c–e.

TEM images of: (a) purified SWCNTs, (b) pure P3HT, the inset image is the sample at higher magnification. (c–e) P3HT/50% SWCNTs at deferent magnifications.

The electrochemical performance of the fabricated supercapacitor electrodes of the pristine P3HT and P3HT/SWCNTs nanocomposites with different ratios are evaluated by CV, GCD and EIS using three-electrode configuration. The CVs (third cycle) are carried out in the potential range from − 0.2 to 1 V vs. Ag/AgCl with different scan rates from 5 to 100 mVs−1 in 0.1 M LiClO4 in acetonitrile as shown in Fig. 5a. The fabricated electrode has a stable shape of CV curves. There is a single oxidation peak located at 1.0 V and one reduction peak at around 0.6 V at scan rate 5 mV/s. This indicates of the Faradic pseudocapacitive nature of the electrode41. However, the voltammograms obtained do not show clearly the anodic peaks and a small reduction peak attributable to the reduction of the film deposited on the electrode. This can be explained based on the participation of capacitive current. The current intensity of the anodic and cathodic peak increases with scan rate. The difference between the oxidation potential and the reduction increases with the scan rate. The proportionality of the peak intensity to the scan rates suggests that the oxidation of electroactive P3HT on the electrode surface is limited by a diffusional process42. For the CV curves of pristine P3HT shown in Fig. 5a, the current increases with scan rate and maintains the shape of CV curves, suggesting that there is a good rate of the capability43.

(a) CV curves of P3HT at different scan rates, (b) CV curves of P3HT/SWCNTs electrodes with different SWCNTs ratios at 50 mV s−1 and (c) CV curves of P3HT/50% SWCNTs at different scan rates.

It is noted that the values of area of the CVs of P3HT/SWCNTs nanocomposites are larger than that of pristine P3HT as shown in Fig. 5b. In addition, there is a slightly effect on SWCNTs addition on the CV behavior due to the nature of electric double layer of the carbon materials. It is observed that the electrochemical supercapacitors containing P3HT component have suffered from relatively large internal resistance44. Figure 5c depicts the CV curves of P3HT/50% SWCNTs nanocomposite at different scan rates. At low scan rates, the ions from the electrolyte can easily diffuse in the microporous surface and bind to the active sites. On the other hand, some active pores on the surface becomes impenetrable for electrolyte ions and charge storage, which describes a decrease in the specific capacitance at high scan rates. Moreover, for this nanocomposite electrode there is a slightly shift in the redox peaks at high scan rates, indicating irreversibility of the electrode materials14,45.

The GCD curves of pure P3HT and P3HT/SWCNTs electrodes at current densities of 0.2, 0.5, 1.0, 1.5 and 2.0 Ag−1 in the potential window range from − 0.2 to 1.0 V vs. Ag/AgCl are illustrated in Fig. 6. In addition, the effect of SWCNTs content in P3HT/SWCNTs electrodes at 0.5 Ag−1 on GCD is displayed and investigated. The curves exhibit semisymmetric triangular shapes and the potential-time relationships are deviated from the linearity, indicating pseudocapacitive contribution and the capacitance of P3HT/SWCNTs originates from pseudocapacitance plus electric double layer capacitance of SWCNTs46. There are two different regions appeared in the discharge curves. Fast potential drop is initially occurred and followed by a slow potential decay. The fast decay is attributed to the internal resistance of the electrode and the latter represents the capacitive feature of the pseudocapacitive electrode46. The nonlinear curves of P3HT/50% SWCNTs electrode at different current densities have pseudocapacitance behavior. Compared with others P3HT/SWCNTs electrodes, P3HT/50% SWCNTs electrode has lower internal resistance and higher pseudocapacitance. Hence the discharge times of P3HT/10% SWCNTs, P3HT/25% SWCNTs and P3HT/50% SWCNTs are 180.45, 343.45 and 589.82 s, respectively. In addition, the GCD curves are not perfectly symmetrically attributed to the electrochemical reversibility of the P3HT/SWCNTs nanocomposite similar to battery-like materials47.

(a) GCD curves of P3HT at different current densities, (b) GCD curves of P3HT/SWCNTs electrodes with different SWCNTs ratios at 0.5 Ag−1 and (c) GCD curves of P3HT/50% SWCNTs at different current densities.

The specific capacitance is calculated from the GCD curves. The P3HT electrodes show that the values of capacitance are declined with increase of the current density (Fig. 6a). From the charge–discharge curves, it is observed that there is a significant effect for SWCNTs ratio in P3HT/SWCNTs nanocomposites on performance of the supercapacitor electrodes as illustrated in Fig. 6b. The electrode based on 50% SWCNTs has a longer discharging time than other ratios in P3HT/SWCNTs nanocomposites. The specific capacitance of P3HT/50% SWCNTs electrode at 0.5 A g−1 is found to be 245.8 Fg−1 while the specific capacitance of pure P3HT electrode is 160.5 Fg−1 (Fig. 6c). These results could be ascribed to the rapid insertion/extraction of electrolyte ions and the voids and pores morphology of the 50% SWCNTs electrode surface. This leads to an enhancement in the effective surface area and the conductivity48. On the other hand, P3HT/10%SWCNTs electrode has a minimum specific capacitance of 75.5 Fg−1 where this electrode has a compact and dense surface as dedicated in the SEM images.

The charge transport and ions diffusion through the fabricated P3HT/SWCNTs electrodes based can be investigated and studied using EIS measurement. Figure 7 illustrates the Nyquist and Bode phase plots of P3HT/SWCNTs electrodes with different SWCNTs ratios in frequency range from 10 kHz to 0.01 Hz. Nyquist plots are analyzed based on the equivalent circuit achieved with Nova software as noted in the inset of Fig. 7a. Rs represents the total resistance of electrolyte and electrode49. The constant phase element (CPE) is pseudocapacitor component, Rct corresponds to the charge transfer resistance and Zw is the Warburg impedance which is attributed to the ions diffusion and electrolyte penetration50,51,52. Nyquist plots exhibit a semi-circle in the high frequency region and a straight part in the low frequency region. This semicircle is attributed to charge transfer resistance at the electrode–electrolyte interface, and the straight line represents the diffusion mechanism of the electrolyte through the electrode surface. It is found that Rs values are 7.9, 27.1, 25.7, and 37.3 Ω for 0%, 10%, 25%, and 50% SWCNTs in P3HT/SWCNTs electrodes, respectively. Rct values of P3HT and P3HT/50% SWCNTs are evaluated to be 17 and 8 Ω, respectively. P3HT/50% SWCNTs electrode at low frequency region displays larger slope than P3HT electrode. The microporous structure of P3HT/50% SWCNTs electrode offers a high surface area and can facilitate rapid ions diffusion and electrolyte penetration in these pores, which improves the specific capacitance50.

Nyquist (a) and Bode phase angle (b) plots of P3HT/SWCNTs electrodes with different SWCNTs ratios.

Bode phase angle plots are the second main format of EIS presentation. The ideal capacitor is expected to have phase angle of 90°. The phase angle of the highest specific capacitance sample (50% SWCNTs) is 55° and is lower than the other samples (Fig. 7b) suggesting a high ionic permeability occurs at low frequencies. Therefore, P3HT/50% SWCNTs electrode is permeable to ions and leads to an increase of the ionic resistance. The capacitor response frequency (f0) is characterized as the position of equal resistive and capacitive, and the relaxation time constant (τ0) is defined as the minimum time for discharging the energy from the supercapacitor. The value of f0 is obtained from the Bode phase angle plots at the position of 45° and τ0 is calculated using the formula of τ0 = 1/f010,53. The relaxation time constant represents the transition from pure resistive to pure capacitive behavior for the electrochemical capacitor. Relaxation times of 0.3, 0.6, 1, and 0.2 s are obtained for the nanocomposite electrodes with 0%, 10%, 25%, and 50% SWCNTs, respectively. These values show that the SC electrodes can be fully discharged within a very short time with an efficiency of more than 50%. Low values of τ suggest that the fast redox reactions result in quick ions transfer between electrodes and electrolyte10,54.

The Ragone plot of specific power density against specific energy density for P3HT/50% SWCNTs electrode is shown in Fig. 8. The obtained curve indicates that the specific power density is declined upon increasing the specific energy density. The energy density is attained about 50.8 Wh kg−1 at a power density of 308.7 W kg−1, which are remarkably high value. In order to represent an actual device, the energy density and power density for three electrodes system are divided by 4 to be equal to 12.7 Wh kg−1 and 77.2 W kg−1, respectively.

Ragone plot of P3HT /SWCNTs assembled nanocomposite supercapacitor electrode.

The long-term stability of the P3HT/50% SWCNTs nanocomposite electrode is examined by GCD cycling at 1 A g−1 as presented in Fig. 9. P3HT/50% SWCNTs electrode keeps the capacitance retention of 80.5% after 1000 cycles. This result indicates that the P3HT/SWCNTs nanocomposite film has long-term cycle stability and could be used as an electrode material for supercapacitors. The stability of pure P3HT during charge–discharge cycles is poor and exhibits a fast decay of specific capacitance due to the degradation of P3HT which occurs mainly due to charge trapping and volume expansion and contraction during intercalation and deintercalation of electrolyte ions into the matrix of the polymer50. In addition, charge trapping is also reduced in the nanocomposites as SWCNTs can act as a current collector. The low stability of P3HT/SWCNTs nanocomposite electrode comes back to the irreversible redox and high Rs value.

Cycling stability of the P3HT/50% SWCNT nanocomposite supercapacitor electrode at 1 A g−1 for 1000 GCD cycles.

The comparison between supercapacitor electrodes previously reported and P3HT/50%SWCNTs electrode are summarized in Table 1. We used a wider potential window and acetonitrile electrolyte than other PHT/SWCNTs electrodes which leads to higher energy density as shown in Table 1.

The fabricated supercapacitor electrodes based on P3HT and SWCNTs nanocomposite with different ratios onto a graphite sheet as substrate were carried out. It was found that P3HT/SWCNTs nanocomposite electrodes possess higher specific capacitance than that of each component. The SEM micrographs of the purified SWCNTs have buckypaper structure while the photomicrographs of P3HT/SWCNTs showed that SWCNTs appeared behind and front of the P3HT nanospheres. The specific capacitance of 50% SWCNTs at a current density of 0.5 Ag−1 was found to be 245.8 F g−1 compared with that of pure P3HT of 160.5 Fg−1.

Purified SWCNTs synthetized by SES Research, Houston, TX 77092, USA was received. Poly (3-hexyl-thiophene-2,5-diyl) was purchased from American Dye Source, Inc, USA. Acetonitrile (99.7%) was obtained from Panreac Químican, Spain. Polyvinylidene difluoride (PVDF) powder was obtained from Alfa Aesar, Canada. Ethanol (99.8%), hydrochloric acid (36%) and chloroform (99.4%) were purchased from Sigma-Aldrich Ltd, UK. All chemicals and solvents were of analytical grade and were used without further purification. Graphite sheet with carbon ratio more than 99.5%, density of 1.1 g cm−3 and thickness of 0.3 mm was purchased from XRD carbon, China.

Graphite sheet was cut to small rectangular shapes with an area of 1 cm2. This sheet was treated with 0.1 M HCl in ultrasonic bath for 15 min and washed by ethanol with ultrasonication for 10 min to remove the acid residuals. Subsequently, these sheets were dried at 60 °C for 15 min. The nanocomposite working electrodes were prepared by mixing different amounts of P3HT and SWCNTs as active materials (90%) with 10% PVDF in 1 mL of chloroform, and then subjected to ultrasonication for about 1 h. Next, 20 µL of the resulting homogeneous solution was placed onto the surface of the graphite sheet and dried at 60 °C.

The morphologies of P3HT, SWCNTs and P3HT/SWCNTs composites were characterized by scanning electron microscopy (SEM, JSM-IT200) operated at 20 kV, and transmission electron microscope (HRTEM, JEOL JEM 2100F) at an accelerating voltage of 200 kV. FTIR spectrophotometer (PerkinElmer-Spectrum 2B, USA) was used to identify the structures and function groups of P3HT and P3HT/SWCNTs nanocomposites pressed with KBr. Raman spectrometer (Senterra Bruker, Germany) was used at excitation wavelength of 532 nm.

In traditional three-electrode system, the electrochemical performance of P3HT/SWCNTs electrode was tested in 0.1 M LiClO4 electrolyte (CH3CN as the supporting electrolyte) using OrigaFlex-OGF05 (Origalys, France) electrochemical workstation in which platinum was used as a counter electrode and Ag/AgCl was used as a reference electrode. The potential window for CV tests is from − 0.2 to 1.0 V vs Ag/AgCl at scan rates ranging from 5 to 100 mV s−1. At the same potential window GCD was conducted at a current density ranging from 0.5 to 2 Ag−1. EIS was measured in the frequency ranging from 10–2 to 106 Hz with amplitude of 5 mV at open circuit potential. The related supercapacitor parameters were calculated by the following equations as below61:

where C, I, and Δt are the specific capacitance (F g−1), the charge/discharge current (A), and the discharge time (s). In addition, m is the mass of active material for a single electrode (g), ΔV is the potential window value (V), E is the energy density (Wh kg−1) and P is the power density (W kg−1). For three electrode system C, E, and P should be dived by 4 to represent an actual device62.

All data included in this study are available upon reasonable request by contact with the corresponding author (A.S.).

Ahn, S. et al. Synergistic molecular engineering of hole-injecting conducting polymers overcomes luminescence quenching in perovskite light-emitting diodes. Adv. Opt. Mater. 9, 2100646–2100654 (2021).

Article CAS Google Scholar

Ebrahim, S. M., Gad, A. & Morsy, A. Highly crystalline and soluble dodecylbenzene sulfonic acid doped poly(o-toluidine). Synth. Met. 160, 2658–2663 (2010).

Article CAS Google Scholar

Shokry, A., El-Tahan, A., Ibrahim, H., Soliman, M. & Ebrahim, S. Polyaniline/akaganéite superparamagnetic nanocomposite for cadmium uptake from polluted water. Desalin. Water Treat. 171, 205–215 (2019).

Article CAS Google Scholar

Shokry, A., Khalil, M., Ibrahim, H., Soliman, M. & Ebrahim, S. Acute toxicity assessment of polyaniline/Ag nanoparticles/graphene oxide quantum dots on Cypridopsis vidua and Artemia salina. Sci. Rep. 11, 5336 (2021).

Article ADS CAS PubMed PubMed Central Google Scholar

Sephra, P. J., Baraneedharan, P. & Arulraj, A. Nanoelectronics devices (field-effect transistors, electrochromic devices, light-emitting diodes, dielectrics, neurotransmitters). In Advances in Hybrid Conducting Polymer Technology (eds Shahabuddin, S. et al.) 77–100 (Springer, 2021).

Chapter Google Scholar

Ebrahim, S., Shokry, A., Khalil, M., Ibrahim, H. & Soliman, M. Polyaniline/Ag nanoparticles/graphene oxide nanocomposite fluorescent sensor for recognition of chromium (VI) ions. Sci. Rep. 10, 13617 (2020).

Article ADS CAS PubMed PubMed Central Google Scholar

El Nady, J. et al. One-step electrodeposition of a polypyrrole/NiO nanocomposite as a supercapacitor electrode. Sci. Rep. 12, 3611 (2022).

Article ADS PubMed PubMed Central CAS Google Scholar

Ebrahim, Sh. M. Fabrication of Schottky diode based on Zn electrode and polyaniline doped with 2-acrylamido-2-methylpropane sulfonate sodium salt. J. Polym. Res. 16, 481–487 (2009).

Article CAS Google Scholar

Awata, R., Shehab, M., El Tahan, A., Soliman, M. & Ebrahim, S. High performance supercapacitor based on camphor sulfonic aciddoped polyaniline/multiwall carbon nanotubes nanocomposite. Electrochim. Acta 347, 136229 (2020).

Article CAS Google Scholar

Da Silva, L. M. et al. Reviewing the fundamentals of supercapacitors and the difficulties involving the analysis of the electrochemical findings obtained for porous electrode materials. Energy Storage Mater. 27, 555–590 (2019).

Article Google Scholar

Moustafa, E., El Nady, J., Kashyout, A. B., Shoueir, K. & El-Kemary, M. Fabrication of high yield photoluminescent quantized graphene nanodiscs for supercapacitor devices. ACS Omega 6, 23090–23099 (2021).

Article CAS PubMed PubMed Central Google Scholar

Elessawy, N. A., El Nady, J., Wazeer, W. & Kashyout, A. B. Development of high-performance supercapacitor based on a novel controllable green synthesis for 3D nitrogen doped graphene. Sci. Rep. 9, 1129 (2019).

Article ADS PubMed PubMed Central CAS Google Scholar

Elsonbaty, A. et al. Novel ZIF67/Mn/MWCNTs decorated with layer double hydroxide supercapacitor electrodes. Electrochim. Acta 368, 137577 (2021).

Article CAS Google Scholar

Elsonbaty, A., Harb, M., Soliman, M., Ebrahim, S. & Eltahan, A. Metal organic framework/layer double hydroxide/graphene oxide nanocomposite supercapacitor electrode. Appl. Phys. Lett. 118, 023901 (2021).

Article ADS CAS Google Scholar

Sowmiya, G. & Velraj, G. Designing a ternary composite of PPy-PT/TiO2 using TiO2, and multipart-conducting polymers for supercapacitor application. J. Mater. Sci. Mater. Electron. 31, 14287–14294 (2020).

Article CAS Google Scholar

Vijeth, H. et al. Flexible and high energy density solid-state asymmetric supercapacitor based on polythiophene nanocomposites and charcoal. RSC Adv. 8, 31414 (2018).

Article ADS Google Scholar

Liu, C., Yu, Z., Neff, D., Zhamu, A. & Jang, B. Z. Graphene-based supercapacitor with an ultrahigh energy density. Nano Lett. 10, 4863–4868 (2010).

Article ADS CAS PubMed Google Scholar

Hu, R., Zhao, J., Zhu, G. & Zheng, J. Fabrication of flexible free-standing reduced graphene oxide/polyaniline nanocomposite film for all-solid-state flexible supercapacitor. Electrochim. Acta 261, 151–159 (2018).

Article CAS Google Scholar

Yuksel, R., Alpugan, E. & Unalan, H. E. Coaxial silver nanowire/polypyrrole nanocomposite supercapacitors. Org. Electron. 52, 272–280 (2018).

Article CAS Google Scholar

Norizan, M. N. et al. Carbon nanotubes: Functionalisation and their application in chemical sensors. RSC Adv. 10, 43704–43732 (2020).

Article ADS CAS PubMed PubMed Central Google Scholar

Jiao, H., Wang, J., Tu, J., Lei, H. & Jiao, S. Aluminum-ion asymmetric supercapacitor Incorporating carbon nanotubes and an ionic liquid electrolyte: Al/AlCl3-[EMIm]Cl/CNTs. Energy Technol. 4, 1112–1118 (2016).

Article CAS Google Scholar

Antiohos, D. et al. Compositional effects of PEDOT-PSS/single walled carbon nanotube films on supercapacitor device performance. J. Mater. Chem. 21, 15987–15994 (2011).

Article CAS Google Scholar

Dhibar, S., Bhattacharya, P., Ghosh, D., Hatui, G. & Das, C. K. Graphene–single-walled carbon nanotubes–poly(3-methylthiophene) ternary nanocomposite for supercapacitor electrode materials. Ind. Eng. Chem. Res. 53, 13030–13045 (2014).

Article CAS Google Scholar

Yang, S. et al. Composite films of poly(3-hexylthiophene) grafted single-walled carbon nanotubes for electrochemical detection of metal ions. ACS Appl. Mater. Interfaces 6, 7686–7694 (2014).

Article CAS PubMed Google Scholar

Li, Y. et al. Polythiophene grafted onto single-wall carbon-nanotubes via oligo(ethylene oxide) linkages for supercapacitor devices with enhanced electrochemical performance. ChemElectroChem 6, 4595–4607 (2019).

Article CAS Google Scholar

Abdou, M. S. A. & Holdcroft, S. Mechanisms of photodegradation of poly(3-alkylthiophenes) in solution. Macromolecules 26, 2954–2962 (1993).

Article ADS CAS Google Scholar

Barrett, H. P., Kennedy, W. J. & Boucher, D. S. Spectroscopic characterization of P3HT/SWNT composites synthesized using in situ GRIM methods: Improved polymer ordering via nanoscaffolding. J. Polym. Sci. B Polym. Phys. 52, 310–320 (2014).

Article ADS CAS Google Scholar

Furukawa, Y., Akimoto, M. & Harada, I. Vibrational key bands and electrical conductivity of polythiophene. Synth. Met. 18, 151–156 (1987).

Article CAS Google Scholar

Li, Y. et al. Remarkably enhanced performances of novel polythiophene-grafting-graphene oxide composite via long alkoxy linkage for supercapacitor application. Carbon 147, 519–531 (2019).

Article CAS Google Scholar

Shi, G., Xu, J. & Fu, M. Raman spectroscopic and electrochemical studies on the doping level changes of polythiophene films during their electrochemical growth processes. J. Phys. Chem. B 106(2), 288–292 (2002).

Article CAS Google Scholar

Voiry, D., Roubeau, O. & Pénicaud, A. Stoichiometric control of single walled carbon nanotubes functionalization. J. Mater. Chem. 20, 4385 (2010).

Article CAS Google Scholar

Hof, F., Bosch, S., Eigler, S., Hauke, F. & Hirsch, A. New basic insight into reductive functionalization sequences of single walled carbon nanotubes (SWCNTs). J. Am. Chem. Soc. 135, 18385–18395 (2013).

Article CAS PubMed Google Scholar

Raïssi, M., Vignau, L., Cloutet, E. & Ratier, B. Soluble carbon nanotubes/phthalocyanines transparent electrode and interconnection layers for flexible inverted polymer tandem solar cells. Org. Electron. 21, 86–91 (2015).

Article CAS Google Scholar

Rao, A. M., Eklund, P. C., Bandow, S., Thess, A. & Smalley, R. E. Evidence for charge transfer in doped carbon nanotube bundles from Raman scattering. Nature 388, 257–259 (1997).

Article ADS CAS Google Scholar

Dresselhaus, M. S., Dresselhaus, G., Saito, R. & Jorio, A. Raman spectroscopy of carbon nanotubes. Phys. Rep. 409, 47–99 (2005).

Article ADS Google Scholar

Chen, Y. et al. Chiral structure determination of aligned single-walled carbon nanotubes on graphite surface. Nano Lett. 13, 5666–5671 (2013).

Article ADS CAS PubMed Google Scholar

Jorio, A. et al. Structural (n, m) determination of isolated single-wall carbon nanotubes by resonant Raman scattering. Phys. Rev. Lett. 86, 1118–1121 (2001).

Article ADS CAS PubMed Google Scholar

Stando, G. et al. Tuning wettability and electrical conductivity of single-walled carbon nanotubes by the modified Hummers method. Sci. Rep. 12, 4358 (2022).

Article ADS CAS PubMed PubMed Central Google Scholar

Rosario-Castro, B. I. et al. Combined electron microscopy and spectroscopy characterization of as-received, acid purified and oxidized HiPCO single-wall carbon nanotubes. Mater. Charact. 60, 1442–1453 (2009).

Article CAS Google Scholar

Husain, A., Ahmad, S., Shariq, M. U. & Khan, M. M. A. Ultra-sensitive, highly selective and completely reversible ammonia sensor based on polythiophene/SWCNT nanocomposite. Materialia 10, 100704–100711 (2020).

Article CAS Google Scholar

Thakur, A. K., Majumder, M., Choudhary, R. B. & Pimpalkar, S. N. Supercapacitor based on electropolymerized polythiophene and multiwalled carbon nanotubes composites. Mater. Sci. Eng. 149, 012166–012175 (2016).

Google Scholar

Maouche, N. & Nessark, B. Cyclic voltammetry and impedance spectroscopy behavior studies of polyterthiophene modified electrode. Int. J. Electrochem. 2011, 1–5 (2011).

Article CAS Google Scholar

Melo, J. P. et al. Synthesis and characterization of graphene/polythiophene (GR/PT) nanocomposites: Evaluation as high-performance supercapacitor electrodes. Int. J. Electrochem. Sci. 12, 2933–2948 (2017).

Article CAS Google Scholar

Ates, M., Caliskan, S. & Ozten, E. A ternary nanocomposite of reduced graphene oxide, Ag nanoparticle and polythiophene used for supercapacitors. Fuller. Nanotubes Carbon Nanostruct. 26, 360–369 (2018).

Article ADS CAS Google Scholar

Shokry, A., Elshaer, A. M., El Nady, J., Ebrahim, S. & Khalil, M. High energy density and specific capacity for supercapacitor based onelectrochemical synthesized polyindole. Electrochim. Acta 423, 140614 (2022).

Article CAS Google Scholar

Azimi, M., Abbaspour, M., Fazli, A., Setoodeh, H. & Pourabbas, B. Investigation on electrochemical properties of polythiophene nanocomposite with graphite derivatives as supercapacitor material on breath figure-decorated PMMA electrode. J. Electron. Mater. 47, 2093–2102 (2018).

Article ADS Google Scholar

Sui, L. et al. Supercapacitive behavior of an asymmetric supercapacitor based on a Ni(OH)2/XC-72 composite. New J. Chem. 39, 9363–9371 (2015).

Article CAS Google Scholar

Parnell, C. M. et al. Electrochemical deposition of cobalt complex and poly(pyrrole) thin films for supercapacitor electrodes. Sci. Rep. 9, 5650 (2019).

Article ADS PubMed PubMed Central CAS Google Scholar

Wang, Z., Liao, J., Chang, L. & Ren, X. Preparation of polythiophene@Fe3O4 nanocomposites and their electrochemical properties. Energy Sources A Recov. Util. Environ. Eff. https://doi.org/10.1080/15567036.2020.1781980 (2020).

Article Google Scholar

Li, T. et al. Three-dimensional conductive porous organic polymers based on tetrahedral polythiophene for high-performance supercapacitors. New J. Chem. 42, 6247–6255 (2012).

Article Google Scholar

Ebrahim, S., Abd El Latif, M. & Soliman, M. Cyclic voltammetry and impedance analysis of 2-acrylamido-2-methyl-1-propanesulfonic acid sodium salt-doped polypyrrole nanoparticles. Thin Solid Films 518, 4100–4105 (2010).

Article ADS CAS Google Scholar

Ebrahim, S. Impedance spectroscopy of heterojunction solar cell based on polyaniline base-equivalent circuit analysis. Polym. Sci. Ser. A 53, 1217–1226 (2011).

Article CAS Google Scholar

Laschuk, O. N., Easton, B. E. & Zenkina, V. O. Reducing the resistance for the use of electrochemical impedance spectroscopy analysis in materials chemistry. RSC Adv. 11, 27925–27936 (2021).

Article ADS CAS PubMed PubMed Central Google Scholar

Fahim, M., Shah, A. H. A. & Bilal, S. Highly Stable and efficient performance of binder-free symmetric supercapacitor fabricated with electroactive polymer synthesized via interfacial polymerization. Materials 12, 1626 (2019).

Article ADS CAS PubMed Central Google Scholar

Liu, F. et al. Facile processing of free-standing polyaniline/SWCNT film as an integrated electrode for flexible supercapacitor application. ACS Appl. Mater. Interfaces 9, 33791–33801 (2017).

Article CAS PubMed Google Scholar

Wang, K., Zhao, P., Zhou, X., Wu, H. & Wei, Z. Flexible supercapacitors based on cloth-supported electrodes of conducting polymer nanowire array/SWCNT composites. J. Mater. Chem. 21, 16373 (2011).

Article CAS Google Scholar

De Oliveira, A. H. P. & de Oliveira, H. P. Carbon nanotube/polypyrrole nanofibers core–shell composites decorated with titanium dioxide nanoparticles for supercapacitor electrodes. J. Power Sources 268, 45–49 (2014).

Article CAS Google Scholar

Gupta, V. & Miura, N. Polyaniline/single-wall carbon nanotube (PANI/SWCNT) composites for high performance supercapacitors. Electrochim. Acta 52, 1721–1726 (2006).

Article CAS Google Scholar

Yoon, J., Lee, J. & Hur, J. Stretchable supercapacitors based on carbon nanotubes-deposited rubber polymer nanofibers electrodes with high tolerance against strain. Nanomaterials 8, 541 (2018).

Article PubMed Central CAS Google Scholar

Zhang, Y. et al. Electrochemical assembly of homogenized poly(3,4-ethylenedioxythiophene methanol)/SWCNT nano-networks and their high performances for supercapacitor electrodes. Ionics 26, 3631–3642 (2020).

Article CAS Google Scholar

Ramadan, A., Anas, M., Ebrahim, S., Soliman, M. & Abou-Aly, A. I. Polyaniline/fullerene derivative nanocomposite for highly efficient supercapacitor electrode. Int. J. Hydrog. Energy 45, 16254–16265 (2020).

Article CAS Google Scholar

Stoller, M. D. & Ruoff, R. S. Best practice methods for determining an electrode material's performance for ultracapacitors. Energy Environ. Sci. 9, 1294 (2010).

Article CAS Google Scholar

Download references

Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).

Department of Materials Science, Institute of Graduate Studies and Research, Alexandria University, 163 Horrya Avenue, El-Shatby, P.O.Box 832, Alexandria, Egypt

Azza Shokry & Shaker Ebrahim

Physics Department, Faculty of Science, Alexandria University, Moharram Bek, P.O. Box 21511, Alexandria, Egypt

Marwa Karim

Department of Nanotechnology and Composite Materials, Institute of New Materials and Advanced Technology, City of Scientific Research and Technological Applications (SRTA-City), New Borg El Arab City, P.O. Box 21934, Alexandria, Egypt

Marwa Khalil

Electronic Materials Department, Advanced Technology and New Materials Research Institute, City of Scientific Research and Technological Applications (SRTA-City), New Borg El-Arab City, P.O. Box 21934, Alexandria, Egypt

Jehan El Nady

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

A.S.: Conceptualization, Data curation, Formal analysis, Investigation, Methodology, Writing-original draft. M.K.: Contribution in Raman Figures & analysis. M.K.: Conceptualization, Data curation, Formal analysis, Investigation, Methodology. S.E.: Conceptualization, Supervision, Data curation, Formal analysis, Writing—review & editing. J.E.: Conceptualization, Data curation, Formal analysis, Investigation, Methodology, Writing—original draft.

Correspondence to Azza Shokry.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Shokry, A., Karim, M., Khalil, M. et al. Supercapacitor based on polymeric binary composite of polythiophene and single-walled carbon nanotubes. Sci Rep 12, 11278 (2022). https://doi.org/10.1038/s41598-022-15477-z

Download citation

Received: 19 February 2022

Accepted: 24 June 2022

Published: 04 July 2022

DOI: https://doi.org/10.1038/s41598-022-15477-z

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Journal of Materials Science: Materials in Electronics (2023)

Environmental Science and Pollution Research (2022)

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.