Photogenerated cathodic protection properties of Ag/NiS/TiO2 nanocomposites

Scientific Reports volume 12, Article number: 4814 (2022) Cite this article

1056 Accesses

1 Citations

1 Altmetric

Metrics details

TiO2 is a semiconductor material used in photoelectric conversion. In order to improve its light utilization rate, nickel sulfide and silver nanoparticles were synthesized on the surface of titanium dioxide nanowires by simple impregnation-deposition and photoreduction methods. A series of studies were conducted on the cathodic protection effect of Ag/NiS/TiO2 nanocomposites on 304 stainless steel, with additional analyses on the material's morphology, composition, and light absorption characteristics. The results indicate that when the number of nickel sulfide impregnation-deposition cycles is 6, and the silver nitrate photoreduction concentration is 0.1 M, the prepared Ag/NiS/TiO2 nanocomposites can provide the best cathodic protection for 304 stainless steel.

The application of n-type semiconductors to photocathodic protection using sunlight has been a hot topic in recent years. Under the excitation of sunlight, the electrons in the valence band (VB) of the semiconductor material will be excited to the conduction band (CB), generating photogenerated electrons. If the conduction band potential of the semiconductor or nanocomposite is more negative than the self-etching potential of the coupled metal, these photogenerated electrons will be transferred to the surface of the coupled metal. The accumulation of electrons will lead to cathode polarization of the metal, and cathodic protection of the coupled metal will be provided1,2,3,4,5,6,7. Semiconductor materials are theoretically regarded as a nonsacrificial photoanode because the anodic reaction does not decompose the semiconductor materials themselves while is carried out through water oxidation by photogenerated holes or adsorbed organic pollutants1, or the presence of trapping agents captures photogenerated holes. Most importantly, the semiconductor material should have a CB potential that is more negative than the corrosion potential of the protected metal. Only in this way can photogenerated electrons be transferred from the semiconductor's conduction band to the protected metal. Photochemical corrosion resistance studies have focused on inorganic n-type semiconductor materials with wide band gaps (3.0–3.2EV)1,2,3,4,5,6,7, which are only responsive to ultraviolet light (< 400 nm), reducing the availability of light.

In the field of marine anticorrosion, photo-electrochemical cathodic protection technology plays a pivotal role. TiO2 is a kind of semiconductor material with excellent UV-light-absorbing property and photocatalysis performance. However, due to its low light utilization rate, photogenerated electron holes easily compound and cannot be protected under dark-state conditions. Further study is needed to propose reasonable and practical solutions. It has been reported that many surface modification treatments can be applied to improve the photosensitivity of TiO2, such as doping with Fe, N and compositing with Ni3S2, Bi2Se3, CdTe and so on. Therefor, compositing TiO2 with high photoelectric conversion efficiency materials has been widely applied in the field of photogenerated cathodic protection.

Nickel sulfide is a semiconductor material with a narrow band gap width of only 1.24 eV8,9. The narrower the band gap width is, the stronger the utilization ratio of light will be. When nickel sulfide is compounded onto the surface of titanium dioxide, the utilization ratio of light can be widened. Combined with titanium dioxide, the separation efficiency of photogenerated electrons and holes can be improved effectively. Nickel sulfide is widely used in electrocatalytic hydrogen production, batteries, and pollutant degradation8,9,10. However, its application in photocathodic protection has not been reported. In this study, a semiconductor material with a narrow band gap width was chosen for solving the low light utilization efficiency of TiO2. Nickel sulfide and silver nanoparticles were combined on the surface of TiO2 nanowires by impregnation-deposition and photoreduction methods, respectively. The Ag/NiS/TiO2 nanocomposite improves the efficiency of light utilization, which makes the absorption range of light expand from the ultraviolet region to the visible region. Meanwhile, the deposition of silver nanoparticles gives the Ag/NiS/TiO2 nanocomposites excellent optical stability and sustainable cathodic protection.

First, a 0.1 mm thick titanium foil with a purity of 99.9% was cut to a size of 30 mm × 10 mm for the experiment. Then, the titanium foil was polished with 2500-mesh sandpaper 100 times on each surface and then washed with acetone, anhydrous ethanol, and distilled water in turn. The titanium plates were placed in a mixture at 85 °C (sodium hydroxide:sodium carbonate:water = 5:2:100) for 90 min, removed, and cleaned with distilled water. The surface was etched by a HF solution (HF:H2O = 1:5) for 1 min, and then cleaned with acetone, ethanol, and distilled water in turn, finally blow-dried for later use. Titanium dioxide nanowires were rapidly prepared on the surface of titanium foil by one-step anodic oxidation11. A traditional two-electrode system was used for anodic oxidation, the working electrode was a titanium sheet, and the counter electrode was a platinum electrode. The titanium plates were placed into 400 mL of a 2 M sodium hydroxide solution with an electrode clamp. The current of the DC power supply was stable at approximately 1.3 A. The solution temperature was kept at 80 °C for 180 min during the reaction of the system. The titanium sheet was removed, cleaned with acetone and ethanol, cleaned with distilled water, and dried naturally. Then, the sample was placed in a muffle furnace at 450 °C (heating rate of 5 °C/min), kept at a constant temperature for 120 min, and placed in a dry dish.

The composite of nickel sulfide and titanium dioxide was obtained by a simple and easy impregnation-deposition method8. First, nickel nitrate (0.03 M) was dissolved in ethanol under magnetic stirring for 20 min to produce an ethanol solution of nickel nitrate. Next, sodium sulfide (0.03 M) was prepared with a mixed methanol solution (methanol:water = 1:1). Then titanium dioxide tablets were put into the above-prepared solution, removed after 4 min, and rinsed quickly with the mixed solution of methanol and water (methanol:water = 1:1) for 1 min. After the surface was dried, the tablet was placed in the muffle furnace under vacuum at 380 °C for 20 min, cooled to room temperature and dried. The number of cycles was 2, 4, 6, and 8.

Silver nanoparticles modified Ag/NiS/TiO2 nanocomposite by photoreduction12,13. The obtained Ag/NiS/TiO2 nanocomposite was put into the silver nitrate solution required for the experiment. Then, the sample was exposed to ultraviolet light for 30 min, its surface was washed clean with deionized water, and the Ag/NiS/TiO2 nanocomposite was obtained by natural drying. The above experimental process is shown as Fig. 1.

Schematic diagram of the procedures used to prepare the Ag/NiS/TiO2 nanocomposite.

The Ag/NiS/TiO2 nanocomposite was mainly characterized by field-emission scanning electron microscopy (FESEM), energy dispersive spectroscopy (EDS), X-ray photoelectron spectroscopy (XPS), and UV–visible diffuse reflectance (UV–Vis). FESEM was performed using a Nova NanoSEM 450 microscope (FEI Company, USA). Its acceleration voltage is 1 kV, and spot size is 2.0. The equipment uses a CBS probe to receive secondary electrons and backscattered electrons to analyze the morphology. EDS was performed with an Oxford X-Max N50 EDS system (Oxford Instruments Technology Co., Ltd.) with an acceleration voltage of 15 kV and a spot size of 3.0. Qualitative and quantitative analyses were conducted with characteristic X-ray. X-ray photoelectron spectroscopy was performed using an Escalab 250Xi spectrometer (Thermo Fisher Scientific Corporation, USA) operated in fixed energy mode with an excitation power of 150 W, monochromatic Al Kα radiation (1486.6 eV) were used as the excitation source. Full scanning range of 0–1600 eV, general energy of 50 eV, step width of 1.0 eV, and contaminated carbon (~ 284.8 eV) were used as the binding energy charge correction reference. The pass energy of the narrow scan was 20 eV, and the step width was 0.05 eV. UV–visible diffuse reflectance spectroscopy was performed with a Cary 5000 spectrometer (Varian, USA) with a barium sulfate reference plate and a scanning range of 10°–80°.

In this work, the composition (wt.%) of 304 stainless steel was 0.08 C, 1.86 Mn, 0.72 Si, 0.035 P, 0.029 s, 18.25 Cr, 8.5 Ni, and with Fe forming the remainder. The 304 stainless steel with dimensions of 10 mm × 10 mm × 10 mm was sealed with epoxy resin, leaving the exposed surface area 1 cm2. Its surface was polished with 2400 mesh silicon carbide sandpaper and washed with ethanol. Afterward, the stainless steel was ultrasonicated in deionized water for 5 min, then stored in a drying dish.

During the OCP experiment, the 304 stainless steel and Ag/NiS/TiO2 photoanode were placed in the corrosion pool and photoanode cell, respectively (Fig. 2). The corrosion cell was filled with 3.5% NaCl solution whereas the 0.25 M Na2SO3 was filled into the photoanode cell as a hole trapping agent. A naphthol membrane was used to separate the two electrolytes from mixing. OCP was measured by an electrochemical workstation (P4000+, USA). The reference electrode was a saturated calomel electrode (SCE). The light source (xenon lamp, PLS-SXE300C, Poisson Technologies Co., Ltd.) and 420 cut-off plates were placed at the outlet of the light source so that visible light reached the optical anode through quartz glass. The 304 stainless steel electrode was connected with the photoanode by a copper wire. Before the experiment, the 304 stainless steel electrode was immersed in a 3.5% NaCl solution for 2 h to ensure that the steady state was achieved. At the beginning of the experiment, by opening and closing the light, the excited electrons of the photoanode will reach the surface of 304 stainless steel through the wire. After switching on the light, the OCP of 304 stainless steel was recorded.

Schematic illustration of the experimental set-up for measuring photoinduced potential.

During the photoinduced current density experiment, 304SS and Ag/NiS/TiO2 photoanode were placed in the corrosion cell and photoanode cell, respectively (Fig. 3). The photocurrent density was measured with the same apparatus as OCP. To obtain the actual photocurrent density between 304 stainless steel and photoanode, the potentiostat was adopted as a zero-resistance ammeter that connected between 304 stainless steel and photoanode under a non-polarization condition. In order to achieve this goal, the reference electrode and the counter electrode are short-connected in the experimental device, so that the electrochemical workstation is like a zero-resistance ammeter, and the true current density can be measured. The 304 stainless steel electrode is connected to the grounding position of the electrochemical workstation, and the photoanode is connected to the working electrode clip. At the beginning of the experiment, by opening and closing the light, the excited electrons of the photoanode will reach the surface of 304 stainless steel through the wire. At this time, the change of the photocurrent density on the surface of 304 stainless steel can be observed.

Schematic illustrations of the experimental set-up for measuring photoinduced current density.

In order to investigate the cathodic protection performance of nanocomposite on 304 stainless steel, the change in the photoionization potential of 304 stainless steel coupled with nanocomposite and the change in photoionization current density between the nanocomposite and 304 stainless steel were tested.

Figure 4 shows the open-circuit potential variation of 304 stainless steel coupled with nanocomposites under visible light irradiation and dark state conditions. Figure 4a shows the influence of nickel sulfide impregnation-deposition times on the open-circuit potential, while Fig. 4b shows the influence of the silver nitrate concentration on the open-circuit potential during photoreduction. Figure 4a shows that compared to the nickel sulfide composite, the open-circuit potential of NiS/TiO2 nanocomposite coupled with 304 stainless steel is significantly reduced at the moment that the lamp is opened. In addition, the open-circuit potential is more negative than that of pure titanium dioxide nanowire, indicating that the nickel sulfide composite produces more electrons and improves the photocathodic protection effect of titanium dioxide. However, when light exposure ends, the open-circuit potential rises rapidly to the open-circuit potential of stainless steel, indicating that nickel sulfide does not have an energy storage effect. The influence of the number of impregnation-deposition cycles on the open-circuit potential can be observed in Fig. 4a. When the deposition time is 6, the extreme electrical potential of the nanocomposite reaches − 550 mV relative to the saturated calomel electrode, and the potential of the nanocomposite deposited 6 times is significantly more negative than that of the nanocomposite under other conditions. Thus, the NiS/TiO2 nanocomposite obtained after 6 deposition cycles provides the best cathodic protection for 304 stainless steel.

OCP variations of the 304 SS electrode coupled with the NiS/TiO2 nanocomposite (a) and Ag/NiS/TiO2 nanocomposite (b) with and without illumination (λ > 400 nm).

As shown in Fig. 4b, when light is applied, the open-circuit potential of 304 stainless steel coupled with Ag/NiS/TiO2 nanocomposite was significantly reduced. After surface deposition of silver nanoparticles, the open-circuit potential was significantly reduced compared with pure TiO2 nanowires. The NiS/TiO2 nanocomposite potential was more negative, showing that the cathodic protection effect of titanium dioxide improves significantly after the deposition of silver nanoparticles. The open-circuit potential increases rapidly when light exposure ends, compared with the saturated calomel electrode, the open-circuit potential can reach − 580 mV, which is lower than 304 stainless steel's potential (− 180 mV). This result shows that the nanocomposites have a noticeable energy storage effect after the deposition of silver particles on their surfaces. Figure 4b also shows the influence of the silver nitrate concentration on the open-circuit potential. When the concentration of silver nitrate is 0.1 M, the electric extreme potential relative to the saturated calomel electrode reaches − 925 mV. After 4 application cycles, the potential remained at the level after the first application, indicating that the nanocomposite has excellent stability. Thus, when the concentration of silver nitrate was 0.1 M, the Ag/NiS/TiO2 nanocomposite obtained provided the best cathodic protection for 304 stainless steel.

With the increase in the deposition times of nickel sulfide, the deposition of nickel sulfide on the surface of titanium dioxide nanowires gradually improved. When visible light irradiated the surface of the nanowires, more nickel sulfide active sites were excited to generate electrons, and the photoionization potential decreased more. However, when too many nickel sulfide nanoparticles are deposited on the surface, the excited nickel sulfide decreases instead, which is not conducive to light absorption3. After the silver particles are deposited on the surface, due to the surface plasmon resonance effect of the silver particles, the generated electrons will quickly transfer to the surface of 304 stainless steel, producing an excellent cathodic protection effect. When too many silver particles are deposited on the surface, the silver particles will become the composite point of photoelectrons and holes, which is adverse to the production of photoelectrons14. In summary, the Ag/NiS/TiO2 nanocomposite can provide the best cathodic protection for 304 stainless steel after 6 nickel sulfide depositions at 0.1 M of silver nitrate.

The magnitude of the photocurrent density represents the separation ability of photogenerated electrons and holes, and a more significant photocurrent density represents a stronger separation ability of photogenerated electrons and holes. There are many studies showing that NiS has been widely used in synthetic photocatalytic materials to improve the ability of material optoelectronics and hole separation15,16,17,18,19,20. The noble-metal-free graphene and NiS co-modified g-C3N4 composite was studied by Chen et al.15. The maximum photocurrent intensity of the modified g-C3N4/0.25%RGO/3%NiS was 0.018 µA/cm2. The photocurrent density of CdSe-NiS with a value of about 10 µA/cm2 was studied by Chen et al.16. The CdS@NiS composites with a 15 µA/cm2 photocurrent density was synthesized by Liu et al.18. However, NiS applied in photocathodic protection has not been reported. In our study, the photocurrent density of TiO2 is significantly improved by NiS modification. Figure 5 shows the variation in the photocurrent densities of 304 stainless steel and nanocomposite under visible and no illumination conditions. As shown in Fig. 5a, the photocurrent density of the NiS/TiO2 nanocomposite increases rapidly at the moment when the light is switched on, and the photocurrent density is positive, indicating that electrons flow from the nanocomposite through the electrochemical workstation to the surface of 304 stainless steel. After the nickel sulfide composite is prepared, the photocurrent density is more substantial than that of pure titanium dioxide nanowires. The photocurrent density of nickel sulfide reached 220 μA/cm2, 6.8 times higher than that of titanium dioxide nanowires (32 μA/cm2) when the number of nickel sulfide immersion and deposition was 6. As shown in Fig. 5b, upon turning on the xenon lamp, the photocurrent density between the Ag/NiS/TiO2 nanocomposite and 304 stainless steel was significantly higher than that between pure titanium dioxide and the NiS/TiO2 nanocomposite. Figure 5b also shows the influence of the concentration of silver nitrate on the photocurrent density during the photoreduction process. When the concentration of silver nitrate is 0.1 M, its photocurrent density reaches 410 μA/cm2, which is 12.8 times the photocurrent density generated by titanium dioxide nanowires (32 μA/cm2) and 1.8 times that of the NiS/TiO2 nanocomposite. A heterogeneous junction electric field forms at the Ag/NiS/TiO2 nanocomposite interface, making it easier to separate photogenerated electrons from holes.

Photocurrent density variations of the 304 SS electrode coupled with the NiS/TiO2 nanocomposite (a) and Ag/NiS/TiO2 nanocomposite (b) with and without illumination (λ > 400 nm).

In summary, through 6 nickel sulfide maceration-deposition cycles under 0.1 M concentrated silver nitrate, the photocurrent density between the Ag/NiS/TiO2 nanocomposite and 304 stainless steel reached 410 μA/cm2, and the extreme electrical potential relative to the saturated calomel electrode reached − 925 mV. Under such conditions, 304 stainless steel coupled with Ag/NiS/TiO2 could provide the best cathodic protection.

Figure 6 shows the surface electron microscopy images of pure titanium dioxide nanowire, nickel sulfide composite nanoparticle, and silver nanoparticle under optimal conditions. Figure 6a,d show the pure titanium dioxide nanowire prepared by one-step anodic oxidation. The surface distribution of titanium dioxide nanowire is uniform, the nanowire structures are close to each other, and the pore size distribution is uniform. Figure 6b,e are titania electron micrographs of nickel sulfide composites impregnated-deposited 6 times. From Fig. 6e of electron microscopy images taken at 200,000 times magnification, we can see that the nickel sulfide composite nanoparticles are relatively uniform, and their particle size is relatively large, their diameter is approximately 100–120 nm. Some nanoparticles can be observed in the nanowire space position, and titanium dioxide nanowires are clearly visible. Figure 6c,f show the electron microscopy images of the NiS/TiO2 nanocomposite when the concentration of silver nitrate was 0.1 M. Comparing with Fig. 6b and Fig. 6e, Fig. 6c and Fig. 6f show that silver nanoparticles are deposited on the surface of the composite, the distribution of silver nanoparticles is uniform, and that their diameter is approximately 10 nm. Figure 7 shows the cross-section of Ag/NiS/TiO2 nanofilms with 6 NiS impregnation-deposition cycles performed at a AgNO3 concentration of 0.1 M. From the higher-magnification image, the film thickness is measured to be 240–270 nm. In summary, nickel sulfide and silver nanoparticles composite on the surface of titanium dioxide nanowires.

SEM images of pure TiO2 (a,d), NiS/TiO2 nanocomposite with 6 NiS impregnation-deposition cycles (b,e) and Ag/NiS/TiO2 nanocomposite with 6 NiS impregnation-deposition cycles performed at a AgNO3 concentration of 0.1 M (c,f).

Cross-section of Ag/NiS/TiO2 nanofilms with 6 NiS impregnation-deposition cycles performed at a AgNO3 concentration of 0.1 M.

Figure 8 shows the elemental surface distribution of the Ag/NiS/TiO2 nanocomposite obtained by performing 6 nickel sulfide impregnation-deposition cycles at a silver nitrate concentration of 0.1 M. The elemental surface distribution shows that the energy spectrum detects Ti, O, Ni, S, and Ag. In terms of content, Ti and O are the most abundant elements in the distribution, while the Ni and S contents are approximately the same, but their contents are significantly less than the Ag content. It can also be proven that the number of composite silver nanoparticles on the surface is greater than that of nickel sulfide. The uniform distribution of each element on the surface indicates that nickel sulfide and silver are uniformly combined on the surface of titanium dioxide nanowires. To analyse the specific composition and the combination state of the substance, we further performed X-ray photoelectron spectroscopy.

Elemental distributions (Ti, O, Ni, S and Ag) of the Ag/NiS/TiO2 nanocomposite with 6 NiS impregnation-deposition cycles performed at a AgNO3 concentration of 0.1 M.

Figure 9 shows the XPS spectra of the Ag/NiS/TiO2 nanocomposite prepared by performing 6 nickel sulfide impregnation-deposition cycles at 0.1 M of silver nitrate., in which Fig. 9a is the full spectrum, and the other spectra are the high-resolution spectra of the elements. As seen from the full spectrum of Fig. 9a, absorption peaks of Ti, O, Ni, S and Ag were detected in the nanocomposite material, and the existence of these five elements was proven. The detection results were consistent with those of EDS. The redundant peaks in Fig. 9a are the carbon peaks used to correct the binding energy of the sample. Figure 9b shows the high-resolution Ti energy spectrum. The absorption peaks of the 2p orbital are located at 459.32 and 465 eV, and the absorption peaks at these two places correspond to the absorption of Ti 2p3/2 and Ti 2p1/2 orbitals1. The two absorption peaks prove that the valence of titanium is Ti4+, corresponding to Ti in TiO2.

XPS survey spectra of Ag/NiS/TiO2 (a) and high-resolution Ti 2p (b), O 1 s (c), Ni 2p (d), S 2p (e) and Ag 3d (f) XPS spectra.

Figure 9d shows the high-resolution Ni energy spectrum, and there are four absorption peaks for the Ni 2p orbital. The absorption peaks at 856 and 873.5 eV correspond to Ni 2p3/2 and Ni 2p1/2 orbitals8,10, where the absorption peaks are derived from NiS. The absorption peaks at 881 and 863 eV were derived from nickel nitrate and were caused by the nickel nitrate reagent during sample preparation. Figure 9e shows the high-resolution S energy spectra. The absorption peaks of the S 2p orbital are located at 161.5 and 168.1 eV, corresponding to S 2p3/2 and S 2p1/2 orbitals21,22,23,24. These two peaks are attributed to nickel sulfide compounds. The absorption peaks at 169.2 and 163.4 eV were derived from the sodium sulfide reagent. Figure 9f shows the high-resolution Ag energy spectrum, in which the 3d orbital absorption peaks of silver are located at 368.2 and 374.5 eV, and the absorption peaks at the two places correspond to the absorption of Ag 3d5/2 and Ag 3d3/2 orbitals12,13. The peaks at these two places prove that silver nanoparticle exist in the elemental silver state. In summary, the nanocomposites are mainly composed of Ag, NiS, and TiO2, as determined by X-ray photoelectron spectroscopy, proving that nickel sulfide and silver nanoparticles are successfully composited on the surface of titanium dioxide nanowires.

Figure 10 shows the UV–Vis diffuse reflectance spectra of the as-prepared titanium dioxide nanowires, NiS/TiO2 nanocomposites, and Ag/NiS/TiO2 nanocomposites. As seen from the figure, the absorption threshold of titanium dioxide nanowires is approximately 390 nm, and the absorbed light is mainly concentrated on the ultraviolet region. The figure shows that the light adsorbed extends to the visible region after nickel sulfide and silver nanoparticles are composite on the surface of21,22 titanium dioxide nanowires. At the same time, the absorption of ultraviolet light by nanocomposites is enhanced, which is due to the narrow band gap of nickel sulfide. The narrower the band gap is, the lower the energy barrier of the electron transition and the higher the utilization of light. After silver nanoparticles were composited on the NiS/TiO2 surface, the absorption intensity and wavelength of light did not increase significantly, mainly due to the plasma resonance effect on the surface of silver nanoparticles. The absorption wavelength of titanium dioxide nanowires could not be significantly improved compared to nickel sulfide composite nanoparticles with narrow band gap widths. In summary, after nickel sulfide and silver nanoparticles were composited on the surface of titanium dioxide nanowires, their optical absorption properties were significantly enhanced, and the absorption range of light was extended from the ultraviolet region to the visible region, which increased the utilization rate of light and improved the photoelectron generation ability of the material.

UV/Vis diffuse reflectance spectra of the prepared TiO2 NWs, NiS/TiO2 nanocomposite and Ag/NiS/TiO2 nanocomposite.

Figure 11 shows the photochemical corrosion resistance mechanism of the Ag/NiS/TiO2 nanocomposite under visible light irradiation. A feasible diagram of the corrosion resistance mechanism is proposed according to the potential distribution10,21,24 of the silver, nickel sulfide nanoparticle, and the titanium dioxide conduction band. Since the conduction band potential of silver nanoparticles is negative with respect to that of nickel sulfide and the conduction band potential of nickel sulfide is negative compared to that of titanium dioxide, the electron flow direction is approximately Ag → NiS → TiO2 → 304 stainless steel. When light is irradiated on the surface of the nanocomposite materials, silver nanoparticles can rapidly produce photogenerated holes and electrons due to the surface plasmonic resonance effect of silver nanoparticles, and photogenerated electrons rapidly transition from the valence band to the conduction band position due to the excitation of titanium dioxide and nickel sulfide. Since the conductivity of silver nanoparticles is more negative than that of nickel sulfide, the electrons in the CB of silver nanoparticles rapidly transition to the CB of nickel sulfide. The conductance potential of nickel sulfide is more negative than that of titanium dioxide, so the electrons of nickel sulfide and silver conductance quickly accumulate in the CB of titanium dioxide. The generated photogenerated electrons reach the surface of 304 stainless steel through the titanium matrix, and the enriched electrons participate in the cathode oxygen reduction process of 304 stainless steel. This process reduces the cathode reaction and simultaneously inhibits the anodic dissolution reaction of 304 stainless steel, thus achieving 304 stainless steel cathodic protection. Due to the formation of a heterogeneous junction electric field in the Ag/NiS/TiO2 nanocomposite, the conductivity potential of the nanocomposite was pulled to a more negative position, which more effectively improved the cathodic protection effect of 304 stainless steel.

Schematic diagram of the photoelectrochemical anticorrosion process in the Ag/NiS/TiO2 nanocomposites under visible light.

In this paper, nickel sulfide and silver nanoparticles were synthesized on the surface of titanium dioxide nanowires by simple impregnation-deposition and photoreduction methods. A series of studies were conducted on the cathodic protection effect of Ag/NiS/TiO2 nanocomposites on 304 stainless steel. Through morphology characterization, composition analysis and light absorption characteristics analysis, the main conclusions are as follows:

When the number of nickel sulfide impregnation-deposition cycles was 6, and the silver nitrate photoreduction concentration was 0.1 M, the prepared Ag/NiS/TiO2 nanocomposites provided the best cathodic protection for 304 stainless steel. Compared with the saturated calomel electrode, the protective potential reaches − 925 mV, and the protective current reaches 410 µA/cm2.

A heterojunction electric field is formed at the interface of the Ag/NiS/TiO2 nanocomposites, which improves the separation ability of photogenerated electrons and holes. At the same time, it improves the efficiency of light utilization, which makes the absorption range of light expand from the ultraviolet region to the visible region. The nanocomposites will still maintain their initial state after 4 cycles and have good stability.

The Ag/NiS/TiO2 nanocomposite prepared in the experiment has a uniformly dense surface. Nickel sulfide and silver nanoparticles were uniformly composited on the surface of TiO2 nanowires. The composite cobalt ferrite and silver nanoparticles have relatively high purity.

Li, M. C., Luo, S. Z., Wu, P. F. & Shen, J. N. Photocathodic protection effect of TiO2 films for carbon steel in 3% NaCl solutions. Electrochim. Acta 50, 3401–3406 (2005).

Article CAS Google Scholar

Li, J., Lin, C. J., Lai, Y. K. & Du, R. G. Photogenerated cathodic protection of flower-like, nanostructured, N-doped TiO2 film on stainless steel. Surf. Coat. Technol. 205, 557–564 (2010).

Article CAS Google Scholar

Zhou, M. J., Zeng, Z. O. & Zhong, L. Photogenerated cathode protection properties of nano-sized TiO2/WO3 coating. Corros. Sci. 51, 1386–1397 (2009).

Article CAS Google Scholar

Park, H., Kim, K. Y. & Choi, W. Photoelectrochemical approach for metal corrosion prevention using a semiconductor photoanode. J. Phys. Chem. B 106, 4775–4781 (2002).

Article CAS Google Scholar

Shen, G. X., Chen, Y. C., Lin, L., Lin, C. J. & Scantlebury, D. Study on a hydrophobic nano-TiO2 coating and its properties for corrosion protection of metals. Electrochim. Acta 50, 5083–5089 (2005).

Article CAS Google Scholar

Yun, H., Li, J., Chen, H. B. & Lin, C. J. A study on the N, S and Cl-modified nano-TiO2 coatings for corrosion protection of stainless steel. Electrochim. Acta 52, 6679–6685 (2007).

Article CAS Google Scholar

Zhu, Y. F., Du, R. G., Chen, W., Qi, H. Q. & Lin, C. J. Photocathodic protection properties of three-dimensional titanate nanowire network films prepared by a combined sol–gel and hydrothermal method. Electrochem. Commun. 12, 1626–1629 (2010).

Article CAS Google Scholar

Lee, J. H., Kim, S. I., Park, S. M. & Kang, M. A p-n heterojunction NiS-sensitized TiO2 photocatalytic system for efficient photoreduction of carbon dioxide to methane. Ceram. Int. 43, 1768–1774 (2017).

Article CAS Google Scholar

Wang, Q. Z. et al. CuS, NiS as co-catalyst for enhanced photocatalytic hydrogen evolution over TiO2. Int. J. Hydrog. Energy 39, 13421–13428 (2014).

Article CAS Google Scholar

Liu, Y. & Tang, C. Enhancement of photocatalytic H2 evolution over TiO2 nano-sheet films by surface loading NiS nanoparticles. Russ. J. Phys. Chem. A 90, 1042–1048 (2016).

Article CAS Google Scholar

Huang, X. W. & Liu, Z. J. Comparative study of the structure and properties of Ti–O-based nanowire films prepared by anodization and chemical oxidation methods. J. Mater. Sci. Technol. 30, 878–883 (2014).

Article CAS Google Scholar

Li, H., Wang, X. T., Liu, Y. & Hou, B. R. Ag and SnO2 co-sensitized TiO2 photoanodes for protection of 304SS under visible light. Corros. Sci. 82, 145–153 (2014).

Article CAS Google Scholar

Wen, Z. H., Wang, N., Wang, J. & Hou, B. R. Ag and CoFe2O4 co-sensitized TiO2 nanowire for photocathodic protection of 304 SS under visible light. Int. J. Electrochem. Sci. 13, 752–761 (2018).

Article CAS Google Scholar

Bu, Y. Y. & Ao, J. P. A review on photoelectrochemical cathodic protection semiconductor thin films for metals. Green Energy Environ. 2, 331–362 (2017).

Article Google Scholar

Chen, Z., Yang, S. B., Tian, Z. F. & Zhu, B. C. NiS and graphene as dual cocatalysts for the enhanced photocatalytic H2 production activity of g-C3N4. Appl. Surf. Sci. 469, 657–665 (2019).

Article ADS CAS Google Scholar

Chen, R., Ao, Y. H. & Wang, P. F. Enhancing the hydrogen evolution performance of CdS by synergistic effect of Ni doping and SnO2 coupling: Improved efficiency of charge transfer and H2O disassociation. Int. J. Hydrog. Energy 46, 6299–6309 (2021).

Article CAS Google Scholar

Yan, A. H., Shi, X. W., Huang, F., Fujitsuka, M. & Majima, T. Efficient photocatalytic H2 evolution using NiS/ZnIn2S4 heterostructures with enhanced charge separation and interfacial charge transfer. Appl. Catal. B Environ. 250, 163–170 (2019).

Article CAS Google Scholar

Liu, C. F., Liu, Y. Y., Xiang, Z. H., Liu, D. H. & Yang, Q. Y. Bimetallic MOF-derived sulfides with heterojunction interfaces synthesized for photocatalytic hydrogen evolution. Ind. Eng. Chem. Res. 60, 11439–11449 (2021).

Article CAS Google Scholar

Yang, Y. et al. Photocatalytic performance of NiS/CdS composite with multistage structure. ACS Appl. Energy Mater. 3, 7736–7745 (2020).

Article CAS Google Scholar

Arumugam, P., Sengodan, P., Duraisamy, N., Rajendran, R. & Vasudevan, V. An effective strategy to enhance the photocatalytic performance by forming NiS/rGO heterojunction nanocomposites. Ionics 26, 4201–4212 (2020).

Article CAS Google Scholar

Mollavali, M., Falamaki, C. & Rohani, S. High performance NiS-nanoparticles sensitized TiO2 nanotube arrays for water reduction. Int. J. Hydrog. Energy 41, 5887–5901 (2016).

Article CAS Google Scholar

Rajamanickam, D., Dhatshanamurthi, P. & Shanthi, M. Enhanced photocatalytic efficiency of NiS/TiO2 composite catalysts using sunset yellow, an azo dye under day light illumination. Mater. Res. Bull. 61, 439–447 (2015).

Article CAS Google Scholar

Ruan, H. C., Li, Y. F., Qiu, H. Y. & Wei, M. D. Synthesis of porous NiS thin films on Ni foam substrate via an electrodeposition route and its application in lithium-ion batteries. J. Alloy. Compd. 588, 357–360 (2014).

Article CAS Google Scholar

Xin, Y. J. et al. Novel NiS cocatalyst decorating ultrathin 2D TiO2 nanosheets with enhanced photocatalytic hydrogen evolution activity. Mater. Res. Bull. 87, 123–129 (2017).

Article CAS Google Scholar

Download references

This work was supported by the National Natural Science Foundation of China (Nos. 42106051, U2106206, U1706225, 42006046, 2019YFC0312103).

CAS Key Laboratory of Marine Environmental Corrosion and Bio-Fouling, Institute of Oceanology, Chinese Academy of Sciences, No.7 Nanhai Road, Qingdao, 266071, People's Republic of China

Ning Wang, Jing Wang, Yanli Ning, Chengyue Ge, Baorong Hou, Qianyu Zhao & Yiteng Hu

Open Studio for Marine Corrosion and Protection, Pilot National Laboratory for Marine Science and Technology, Qingdao, 266237, People's Republic of China

Ning Wang, Jing Wang, Yanli Ning, Chengyue Ge, Baorong Hou, Qianyu Zhao & Yiteng Hu

Center for Ocean Mega-Science, Chinese Academy of Sciences, No. 7 Nanhai Road, Qingdao, 266071, People's Republic of China

Ning Wang, Jing Wang, Yanli Ning, Chengyue Ge, Baorong Hou, Qianyu Zhao & Yiteng Hu

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

N.W.: Data curation, Writing—Original draft preparation. J.W.: Writing—Reviewing and Editing. Y.N.: Visualization. C.G.: Software, Validation. B.H.: Conceptualization, Methodology. Q.Z.: Software. Y.H.: Investigation.

Correspondence to Jing Wang.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Wang, N., Wang, J., Ning, Y. et al. Photogenerated cathodic protection properties of Ag/NiS/TiO2 nanocomposites. Sci Rep 12, 4814 (2022). https://doi.org/10.1038/s41598-022-08929-z

Download citation

Received: 21 December 2021

Accepted: 14 March 2022

Published: 21 March 2022

DOI: https://doi.org/10.1038/s41598-022-08929-z

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.