Local atomic structure studies of Zr55Cu35Al10 alloy around Tg

Scientific Reports volume 13, Article number: 9207 (2023) Cite this article

Metrics details

As a result of examining the structure of Zr55Cu35Al10 alloy around the glass transition temperature (Tg) using the classical molecular dynamics simulations, it was proven that the atomic bonds in the interconnecting zones (i-zones) became loose with the small amount of energy absorption, and it became free volumes easily when the temperature approached Tg. Instead of i-zones, when clusters were largely separated by free volume networks, the solid amorphous structure was converted into supercooled liquid state, resulting in a sharp strength reduce and the great plasticity change from a limited plastic deformation to superplasticity.

It was thought that the atomic distribution of liquid at the temperature above the liquidus was random and uniform. However, with the development of various detection techniques, it was found that the atoms in the liquid presented short and medium range order. A new glassy metal with long-range disordered atomic arrangements-metallic glasses were often referred to as frozen metallic liquid. The topological model of completely disordered arrangement of atoms has been token for the atomic arrangement model of amorphous alloy for a long time after the discovery of amorphous alloy1,2,3,4,5. The free volume means the volume difference between the completely disordered arrangement of atoms and the ordered arrangement of crystals forms. The fraction of free volumes is often determined by the changes in the volume of amorphous alloys before and after crystallization. The concept of free volume is widely used to explain the physical and mechanical properties of metallic glasses6,7,8,9,10. However, researchers have found that the metallic glasses prepared at different cooling rates own different mechanical properties, and the metallic glassed prepared at different liquid temperatures have different thermal properties and present different crystallization process, which means that the atomic arrangement in the frozen metal liquid is not completely disordered, the frozen tissues under different temperatures should have corresponding short and medium range ordered structure, changing with the cooling rate11,12.

Metallic glasses show extremely high strength close to the theoretical value and an unusually large elastic strain because of their unique structural feature13,14,15. Compared with the aluminum, titanium, copper alloys and steel, the strength of Zr-based metallic glasses is more than twice that of Ti6Al4V and 17-4ss stainless steel. The linear elastic strain is ideally maintained to the yield point, which is more than twice that of ordinary alloys. Although metallic glasses have extremely high mechanical strength and physical properties, their macroscopic plasticity is very low. After the large linear elastic deformation and reaching the yield limit, the metal glass is deformed by highly localized shear band movement16,17,18,19. The thickness of the shear bands is only tens of nanometers. Although there is a large amount of deformation in the sheared zone, the metallic glass breaks only when several or only one shear zone is deformed, so the ductility deformation, which is much less than 1%, is often shown to have broken after reaching the yield limit20,21,22.

An understanding of the structure–property relation is the fundamental goal for the study of atomic structures. How to clarify the relationship between the structural models and physical and mechanical properties of glassy materials is important23,24. Differential scanning calorimetry (DSC) showed 0.79W/g energy absorption during glass transition. Yet, when the Zr-based metallic glass turns into the supercooled liquid state from the amorphous solid at room temperature, it only needs to absorb little energy, accompanied by a sharp strength reduce from 2000 to 70 MPa and the great plasticity change from a limited plastic deformation to superplasticity. How does the low energy absorption change the atomic structure of BMGs and brings liquid-like mechanical properties? The structure–property relations are related to not only the atomic packing geometrically but also the bonding properties among atoms, in which bonding length is one of the most important factors29,30.

Most recently, based on the studies of the atom-bonding lengths and atomic packings of local atomic structures using high-intensity neutron, high energy synchrotron diffraction technologies and molecular dynamics (MD) simulations, the atomic structure of the metallic glasses has been carefully characterized. The icosahedra, identified as the basic local structure in the metallic glasses, is widely studied in recent years. Celtek et al. presented that Al has a much greater effect on the formation of icosahedral short range order (SRO) than Ag and Zr50Cu30Al20 alloy has the best glass forming ability in the Zr50Cu50−xAlx (x = 0, 10, 20, 30, 40, and 50) alloys by conducting MD simulations25,26. Zhang et al. reported that the distorted icosahedra ⟨0, 1, 10, 2⟩ has been identified as the basic SRO in many multicomponent metallic glasses using ab initio MD simulations27. Shimono et al.28 regarded a random network formed with Frank–Kasper clusters surrounded by icosahedral clusters as the basic medium-range order structure in metallic glasses by using MD simulations. In this research, the tight-bond cluster model for the metallic glasses has been adopted29,30,31,32,33,34,35,36,37. The tight‐bond cluster model mainly includes clusters, interconnecting-zones (i-zones) and free volumes, and it can be described as the clusters connected together by i-zones, and free volumes form among the clusters. The concept of the i-zones plays an important role in this model29,30,31. The nearest neighbor atoms are classified into cluster, i-zone, and free volume atomic bonds. In different alloy systems, the quantification of the cluster, the i-zone and the free volume bonding length can be defined by comparing the metallic glass structure with the corresponding crystallization structure obtained from the experiment in accordance with the radius of different elements in a particular system32,33,34,35,36,37. The tight-bond cluster model enables us to quantitatively characterize local atomic structures in amorphous alloys, contributing to explaining the phenomenon mentioned above.

In our work, classical molecular dynamics with embedded atom method (EAM) potentials proposed by Sheng et al. were used to investigate the structures of Zr55Cu35Al10 alloy around the glass transition temperature (Tg)5. In the simulation, the cubic cell with initial arrangement of 16,000 atoms was set, and Zr, Cu and Al atoms were generated in random according to the composition of the alloy, and the initial velocity distribution obeyed the Maxwell Boltzmann distribution. The whole process was carried out in the three-dimensional periodic boundary conditions in the NPT ensemble with a Nose–Hoover thermostat for temperature control and a Nose–Hoover barostat for pressure control. The external pressure is set as zero. Firstly, the initial system temperature was set to 2.5 K, and then the temperature was raised to 2000 K to break the original structure and obtain a balanced liquid structure. After that, the system was cooled at a speed of 1010 K/s to 300 K to obtain the solid amorphous structure. The Tg in the simulation is identified at about 730 K through linearly fitting and extrapolating the two parts of the potential energy (PE) curve in the temperature range of 300–600 K and 900–1200 K, and the structures at the corresponding temperatures around Tg were obtained.

The tight-bond cluster model was used to describe the strength between atoms. The cluster bonds are formed with atoms with strong bonding; the free volume bonds have liquid-like loose bonding; the strength of the i-zone bonds fall in between. By comparing the pair distribution functions (PDFs) for the nearest atom pairs of the as-cast bulk metallic Zr55Cu35Al10 glass with its completely crystallized counterpart measured at the temperature of 15 K, cluster, i-zone and free volume bonds were defined31,32,33. The initial distances for the i-zone bonds are set at least 2.8% larger than their characteristic atomic radii, the initial distances for the free volume bonds are set at 9.6% greater than their characteristic atomic radii and the final positions for the free volume bonds are at the end of the first peaks in the corresponding partial PDFs. In addition, the bond formation energy for different atoms is calculated and expressed as follows:

\(E_{p,\alpha }\) presents the PE which can be obtained from the simulation. \(E_{ref,\alpha }\) is the reference energy for the type \(\alpha\) atom. The crystal PE (hcp Zr, fcc Cu and fcc Al) is used as the reference energy.

Figure 1 shows the comparison of the total and partial PDFs at 300 K (the solid amorphous state) and 800 K (supercooled liquid state). It can be seen from the total and partial PDFs that the main difference exists in the first peak. The first peak strength increases significantly and the peak width decreases at 300 K, meaning that there are more atomic pairs with short bonding length at 300 K and it is more possible to form the atomic pairs with long bonding length near the first peak valley at 800 K. For the partial PDFs (ZrZr, ZrCu, ZrAl, CuCu and CuAl), the peak strength of the PDF curves for unlike atomic pairs (ZrCu, ZrAl, and CuAl) is much stronger than that of the like atomic pairs (ZrZr and ZrCu). The AlAl partial PDF is not presented here because of the low Al concentration and the poor statistics of calculating the AlAl partial PDF. It can be found from Fig. 2 that from 300 to 800 K, the fraction of the i-zone atomic bonds present slight decrease, the fraction of the free volume atomic bonds increases and the fraction of the cluster atomic bonds decreases significantly in the whole system and Zr, Cu and Al-centered atomic pairs, in accordance with difference in the first peak of the PDFs at 300 K and 800 K. For the Al-centered atomic bonds, the fraction of the cluster atomic bonds reaches about 0.68, which is much higher than that of the Zr-centered atomic bonds. The Al content is the least in Zr55Cu35Al10 alloy, but the fraction of Al cluster atomic bonds is the largest, indicating that the bonding between unlike atomic pairs Al–Zr or Al–Cu tend to be strong.

Comparison of total and partial pair distribution functions (PDFs) at 300 K and 800 K.

The variation of the fractions of the cluster, interconnecting zone (i-zone) and free volume atomic bonds from 300 to 800 K in the whole system and Zr, Cu and Al-centered atomic pairs.

Figure 3 shows the fraction and energy distribution of different atomic pairs (Zr–Zr, Zr–Cu, Zr–Al, Cu–Cu, Cu–Al and Al–Al). In this figure, the characteristic position, the starting position of the i-zone atomic bonds and the starting position of the free volume atomic bonds for different atomic pairs are indicated by the red, orange and purple lines respectively. The atomic pairs between the orange line and purple line belong to i-zone atomic bonds, the atomic pairs to the left of the orange line belong to cluster atomic bonds and the atomic pairs to the right of the purple line belong to free volume atomic bonds. The fraction curves basically present Gaussian distribution, and the characteristic position is to the right of the peak position for different atomic pairs. By comparing the fraction curves of 300 K and 800 K, it is found that, the peak position basically unchanges while the peak intensity decreases significantly and the peak width increases, indicating the decrease of cluster atomic bonds and the increase of the free volume atomic bonds. The energy distribution curves are "U"-shaped, decrease firstly and then increase as the distance of the atomic pair increases at 300 K and 800 K. The low energy part is most between the orange line and purple line, corresponding to i-zone atomic bonds. It follows that i-zone is an important part of the structure and its existence can reduce the energy of the system, going a long way towards explaining the above phenomenon.

The change of the fraction and the energy of different atomic pairs (Zr–Zr, Zr–Cu, Zr–Al, Cu–Cu, Cu–Al and Al–Al) as a function of the atomic pair distance at 300 K and 800 K.

The atom arrangements can be "physically" seen in the simulation. Figure 4 shows a cluster with i-zones and free volumes. The center of the cluster is Al, and its nearest surrounding atoms are Zr, which forms Zr–Al pairs, except one Cu–Al pair. The bonds shown by the green bars indicate i-zones, and with red bars are free volumes. The bonds in green bars, as well as those in the red bars are not isolated. They are associated with each other. Such it is easy to find that three bonds in green color have a shared atom, and the same of the red ones. It means that they exist as areas, which are able to form networks in the three dimensional space. The configuration of the i-zone and free volume networks should be very important for metallic glasses.

Al-centered cluster surrounded by i-zones and free volumes in local atomic structure. Cluster bonds is in black color, i-zones in green color, and free volume in red color.

The structures from 300 to 800 K are picked up to make a thorough analysis. By tracking the atoms in the simulation from 300 to 800 K, it is found that all atoms only make a short distance migration leading to the expansion of the system with the shell atoms basically unchanged. When temperature increases from 300 to 800 K, the distance between atomic pairs increases, some of the cluster atomic bonds transform into i-zone atomic bonds, releasing energy, while some i-zone atomic bonds turn into free volume atomic bonds, absorbing energy. The absence of long distance migration of atoms and the transforms among the free volume, i-zone and cluster bonds should be the main reasons why the required energy of changing the structure from solid amorphous state at room temperature to the supercooled liquid is so small. However, the structure has undergone tremendous changes. When the temperature is 300 K, the proportion of cluster atomic bonds is very high, and the proportion of i-zone atomic bonds is much higher than that of free volume atomic bonds. When the temperature reaches 800 K, the fraction of cluster atomic bonds significantly decreases, the proportion of free volume atomic bonds has exceeded the proportion of i-zone atomic bonds. More free volumes are formed by consuming the clusters and i-zones. The clusters are mainly connected by free volumes instead of i-zones, the clusters could move and rotate more easily, forming a viscous liquid state. Therefore, there is a sharp decrease in strength and a sharp increase in plasticity when the temperature is above Tg.

In summary, the transformation of Zr-based alloys from the amorphous solid state to the supercooled liquid state requires very little energy absorption, yet the mechanical properties of Zr-based amorphous alloys have undergone great changes, including a sharp decrease in strength and a sharp increase in plasticity. The strength and plasticity change can be attributed to the variation of the distribution of the i-zones and free volumes around the clusters. When the temperature approaches Tg, the i-zone atomic bonds become looser when gaining a small amount of energies, and easily to become to free volumes. When more clusters are surrounded by free volumes instead of the i-zones, the amorphous structure is then converted to the supercooled liquid structure, which results in the great change in the strength and plasticity since the clusters surrounded by the free volume could move smoothly.

The datasets used and/or analysed during the current study available from the corresponding author on reasonable request.

Jun, W. K., Willens, R. H. & Duwez, P. O. L. Non-crystalline structure in solidified gold–silicon alloys. Nature 187(4740), 869 (1960).

Article ADS Google Scholar

Johnson, W. L. Bulk glass-forming metallic alloys: Science and technology. MRS Bull. 24(10), 42–56 (1999).

Article CAS Google Scholar

Feng, Y. et al. A flexible network polyimides binder for Si/graphite composite electrode in lithium-ion batteries. Int. J. Energy Res. 46(13), 18100–18108 (2022).

Article CAS Google Scholar

Pampillo, C. A. Review of flow and fracture in amorphous alloys. J. Mater. Sci. 10, 1194–1227 (1975).

Article CAS ADS Google Scholar

Cheng, Y. Q., Ma, E. & Sheng, H. W. Atomic level structure in multicomponent bulk metallic glass. Phys. Rev. Lett. 102(24), 245501 (2009).

Article CAS PubMed ADS Google Scholar

Hirata, A. et al. Direct observation of local atomic order in a metallic glass. Nat. Mater. 10(1), 28 (2011).

Article CAS PubMed ADS Google Scholar

Wang, X. H. et al. Influence of ejection temperature on structure and glass transition behavior for Zr-based rapidly quenched disordered alloys. Acta Mater. 116, 370–381 (2016).

Article CAS ADS Google Scholar

Sheng, H. W. et al. Atomic packing and short-to-medium-range order in metallic glasses. Nature 439(7075), 419 (2006).

Article CAS PubMed ADS Google Scholar

Chen, D. et al. Microspherical copper tetrathiovanadate with stable binding site as ultra-rate and extended longevity anode for sodium-ion half/full batteries. Chem. Eng. J. 446, 136772 (2022).

Article CAS Google Scholar

Mu, F. et al. Metal-organic framework-derived rodlike AgCl/Ag/In2O3: A plasmonic Z-scheme visible light photocatalyst. Chem. Eng. J. 415, 129010 (2021).

Article CAS Google Scholar

Miracle, D. B. A structural model for metallic glasses. Nat. Mater. 3(10), 697 (2004).

Article CAS PubMed ADS Google Scholar

Ma, D., Stoica, A. D. & Wang, X. L. Power-law scaling and fractal nature of medium-range order in metallic glasses. Nat. Mater. 8(1), 30 (2009).

Article CAS PubMed ADS Google Scholar

Yu, C. Y. et al. Atomistic approach to predict the glass-forming ability in Zr–Cu–Al ternary metallic glasses. J. Alloys Compd. 627, 48–53 (2015).

Article CAS Google Scholar

Yu, C. Y. et al. First-principles prediction and experimental verification of glass-forming ability in Zr–Cu binary metallic glasses. Sci. Rep. 3, 2124 (2013).

Article CAS PubMed PubMed Central Google Scholar

Huang, Y. et al. Ab initio molecular dynamics simulations of short-range order in Zr50Cu45Al5 and Cu50Zr45Al5 metallic glasses. J. Phys.: Condens. Matter 28(8), 085102 (2016).

PubMed ADS Google Scholar

Chu, W. et al. Generality of abnormal viscosity drop on cooling of CuZr alloy melts and its structural origin. Acta Mater. 196, 690–703 (2020).

Article CAS ADS Google Scholar

Liu, P. et al. Deformation path and springback behavior in double-curved bending at high temperature. J. Mech. Sci. Technol. 33, 4361–4370 (2019).

Article Google Scholar

Yang, G. et al. Short to medium range order and atomic dynamic property within the surface of nanoscale metallic glasses revealed by molecular dynamics simulations. J. Non Cryst. Solids 578, 121348 (2022).

Article CAS Google Scholar

Yu, X., Wang, Z. & Lu, Z. In situ investigation of atmospheric corrosion behavior of copper under thin electrolyte layer and static magnetic field. Microelectron. Reliab. 108, 113630 (2020).

Article CAS Google Scholar

Zhang, W. et al. Microstructure characterization and mechanical behavior of dissimilar friction stir welded Al/Cu couple with different joint configurations. Int. J. Adv. Manuf. Technol. 94, 1021–1030 (2018).

Article Google Scholar

Bian, Z., He, G. & Chen, G. L. Microstructure and mechanical properties of as-cast Zr52.5Cu17.9Ni14.6Al10Ti5 bulky glass alloy. Scr. Mater. 11(43), 1003–1008 (2000).

Article Google Scholar

Di-hua, O. et al. Preparation and the thermal properties of porous barium nitrate. Sci. Technol. Energ. Mater. 82(4), 89–94 (2021).

Google Scholar

Yang, L. et al. Effect of aluminum concentration on the microstructure and mechanical properties of Sn–Cu–Al solder alloy. Microelectron. Reliab. 55(3–4), 596–601 (2015).

Article CAS Google Scholar

Ma, E. Tuning order in disorder. Nat. Mater. 14(6), 547 (2015).

Article CAS PubMed ADS Google Scholar

Celtek, M., Sengul, S. & Domekeli, U. Glass formation and structural properties of Zr50Cu50−xAlx bulk metallic glasses investigated by molecular dynamics simulations. Intermetallics 84, 62–73 (2017).

Article CAS Google Scholar

Celtek, M. et al. Effects of Ag or Al addition to CuZr-based metallic alloys on glass formation and structural evolution: A molecular dynamics simulation study. Intermetallics 128, 107023 (2021).

Article CAS Google Scholar

Zhang, J. C. et al. Ab initio molecular dynamics study of the local atomic structures in monatomic metallic liquid and glass. Mater. Des. 77, 1–5 (2015).

Article Google Scholar

Shimono, M. & Onodera, H. Dual cluster model for medium-range order in metallic glasses. Metals 11(11), 1840 (2021).

Article CAS Google Scholar

Fan, C., Liaw, P. K. & Liu, C. T. Atomistic model of amorphous materials. Intermetallics 17(1–2), 86–87 (2009).

Article CAS Google Scholar

Fan, C. et al. Atomic migration and bonding characteristics during a glass transition investigated using as-cast Zr–Cu–Al. Phys. Rev. B 83(19), 195207 (2011).

Article ADS Google Scholar

Fan, C. et al. Changes in the atomic structure through glass transition observed by X-ray scattering. Intermetallics 23, 111–115 (2012).

Article CAS Google Scholar

Fan, C. et al. Effect of molten quenching temperature on glass-forming ability of nanoquasi-crystal-forming Zr-based metallic glasses. Scripta Mater. 68(7), 534–537 (2013).

Article CAS Google Scholar

Fan, C. et al. Quantitatively defining interconnecting-zone in metallic glasses. Intermetallics 49, 36–39 (2014).

Article CAS Google Scholar

Zhao, J. et al. Structural evolution and energy landscape of the clusters in Zr55Cu35Al10 metallic liquid and glass. Scripta Mater. 117, 64–67 (2016).

Article CAS Google Scholar

Fan, C. et al. Quantitatively defining free-volume, interconnecting-zone and cluster in metallic glasses. Intermetallics 57, 98–100 (2015).

Article CAS Google Scholar

Zhao, J. et al. Evolution of the atomic structure of a supercooled Zr55Cu35Al10 liquid. Intermetallics 82, 53–58 (2017).

Article CAS Google Scholar

Zhao, J. et al. Structural evolution and energy landscape of Zr55Cu35Al10 ternary alloy during glass transition. J. Alloy. Compd. 825, 154109 (2020).

Article CAS Google Scholar

Download references

School of Automotive Engineering, Changshu Institute of Technology, Changshu, 215500, People's Republic of China

Jingfeng Zhao, Yuhang Chen, Chucheng Shao, Jiang Liu & Xuefeng Zhou

Jiangsu Xinxunda Stainless Steel Products Co. LTD, Yancheng, 224000, People's Republic of China

Jingfeng Zhao & Genyu Zhu

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

J.Z. and X.Z. wrote the main manuscript text. Y.C. and C.S. prepared Figures 1 and 2. J.L. prepared Figures 3 and 4. G.Z. modified the manuscript All authors reviewed the manuscript.

Correspondence to Xuefeng Zhou.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Zhao, J., Chen, Y., Shao, C. et al. Local atomic structure studies of Zr55Cu35Al10 alloy around Tg. Sci Rep 13, 9207 (2023). https://doi.org/10.1038/s41598-023-36524-3

Download citation

Received: 30 March 2023

Accepted: 05 June 2023

Published: 06 June 2023

DOI: https://doi.org/10.1038/s41598-023-36524-3

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.