banner

Blog

Jul 04, 2023

Experimental and theoretical studies for corrosion of molybdenum electrode using streptomycin drug in phosphoric acid medium

Scientific Reports volume 13, Article number: 4827 (2023) Cite this article

429 Accesses

4 Altmetric

Metrics details

Corrosion inhibition of molybdenum electrode in H3PO4 acid medium of different concentrations (3.0 to 13 M) has been investigated utilizing different electrochemical techniques. It was observed that the most corrosive concentration is 3.0 M orthophosphoric acid concentration. The effect of adding Cl− to 3.0 M orthophosphoric acid in the concentration range of 0.1 to 1.0 M was also studied. This study showed that the most corrosive medium is 3.0 M containing 1.0 M chloride ion with the greatest rate of hydrogen production. In 3.0 M H3PO4 acid with 1.0 M of NaCl, the tested electrode's corrosion and hydrogen production may be successfully suppressed by adding Streptomycin of 10 mM concentration leading to high inhibition efficiency. The outcomes of the studies were confirmed by scanning electron microscopic examination. Additionally, a computational chemistry approach was used to investigate how streptomycin adsorbs and inhibits corrosion at the interface of metal surfaces, and the outcomes of the computational studies are in excellent accord with the experimental findings.

Recently, studying the deterioration of the metals and alloys is considered an essential process of different approaches. Whereas, metals and alloys are widely used as electrodes in various applications like fuel cells, sensors, solar cells, and batteries1,2,3,4,5. Addition of Molybdenum to Cr–Ni stainless steels affects their properties in many aspects6,7,8,9. In addition, it reduces the risk of passive film deterioration in chloride medium. Hence, it increases passive film thickness, which is, in turn, improves the alloy's resistance for corrosion. For increasing the strength, hardenability, toughness, and wear/corrosion resistance of steels, cast iron, and superalloys, molybdenum (Mo), a refractory metal, is frequently used as an alloying element10,11,12,13. Besides, molybdenum is utilized significantly in numerous chemical applications. It is well-known that the metal's high corrosion protection is attributable to the formation of thin, constant, and unsolvable oxide film of MoO2, which protects the metal surface from further surface oxidation14,15. Therefore, utilization of inhibitors to reduce corrosion of metals in contact with aggressive conditions is crucial, especially compounds containing N, S, or O16,17. A family of green corrosion inhibitors known as antibacterial medications has been proven to slow down the corrosion of engineered materials in a variety of media18.

Streptomycin is a first-line medicine for the treatment of plague that is also frequently used to treat tuberculosis when combined with other medications19. With effective antibacterial action, an aminoglycoside antibiotic called streptomycin produced from Streptomyces griseus20,21,22,23 with inhibitory consequence on Gram-negative bacteria, it is a well-known vet medication for bacterial illnesses and livestock farming24. Therefore, streptomycin as an antibiotic drug, a bactericidal antibiotic, and containing nitrogen and oxygen heteroatoms may be utilized to prevent corrosion in a variety of metals and alloys25. Acid solutions are utilized in numerous engineering applications26,27,28,29,30,31. Qiang et al. studied corrosion inhibition of some metals e.g. steel, copper, …etc. in acidic media27,28,29,30. Qiang et al. investigated the inhibitory effect of Losartan Potassium (LP) drug as a corrosion inhibitor for Q235 steel in hydrochloric acid29. A strong adsorption of LP on Q235 surface was proved by low ΔE and high Ebinding values29. Phosphoric acid is readily used in acid washing applications due to its superior chemical properties. Corrosion inhibitors can reduce and, in several situations, prevent metal corrosion in harsh media by reducing hydrogen formation32,33,34.

The chief purpose herein is to utilize surface examination procedures to investigate the electrochemical performance of molybdenum electrodes in various concentrations of an aerated H3PO4 solutions. Similarly, chloride ion with various concentrations (0.1–1.0 M) to 3.0 M H3PO4 solution was considered. Different levels of Streptomycin concentrations were investigated as an inhibitor for corrosion of molybdenum electrode in 3.0 M H3PO4 acid solution containing 1.0 M sodium chloride additive. The results of the experiment demonstrated that this substance considerably hinders the corrosion at 10−2 M concentrations of streptomycin. A direct relationship was found between the efficiency of corrosion inhibition and the concentration of the inhibitor in the presence of Cl− ions in 3.0 M H3PO4 solution. Computational modeling was performed to validate the experimental results; suitability of Streptomycin as a corrosion inhibitor. This model can be used to extend the study to other concentrations that are not part of the current study. Figure 1 shows a schematic illustration of Streptomycin is as follows.

Schematic illustration of Streptomycin.

A pure molybdenum electrode rod was prepared with a cross-sectional area of 1.0 cm2 in a cylindrical shape connected to a copper cable, covered with an adhesive epoxy resin coating made of Araldite, and injected in a glass cylinder. The electrode was refined by rubbing it with increasingly finer grades of emery paper (600–1600 grade), followed by a triple-distilled water rinse, bathed ultrasonically with acetone, and dehydrated in the air. The working electrode (WE) is a pure molybdenum electrode, platinum sheet and calomel electrode were used as auxiliary and reference electrodes, respectively. The three electrodes are inserted in a 25 ml cell containing the test solution.

The materials utilized are H3PO4, NaCl (Aldrich), and Streptomycin drug (antibiotic). The phosphoric acid solution is prepared in various concentrations (3.0 to 13 M), sodium chloride concentrations are 0.1–1.0 M and the inhibitor concentrations (Streptomycin) are 0.5–10 mM. All preparations used water that had been triple distilled. The electrochemical workstation IM6e from Zahner-electrik GmbH, Metechnik, Kronach, Germany, was employed to estimate electrochemical impedance spectroscopy (EIS) and polarization. The excitation AC voltage for the electrochemical impedance spectroscopy technique had a frequency range of 0.1 Hz to 100 kHz, and a peak-to-peak (p-p) amplitude of 10 mV. In comparison to a saturated calomel electrode, the sweeping rate was 30 mV min−1 across the potential operating voltage of −1000 to 0 mV. The intersecting of Tafel lines extension was implemented to derive the corrosion current density, abbreviated icorr. Using a computer least-squares analysis, the gradient of the points after Ecorr by ± 50 mV was employed to derive Tafel constants. A scanning electron microscope (SEM) of JEOL-JEM-100s type with a 100× magnification was utilized for the surface investigation.

Streptomycin (C21H39N7O12) (molar mass = 581.574 g mol−1) is the first in class drug called aminoglycosides to be discovered25,35. It contains methoxy, amino, and hydroxyl groups.

Potentiodynamic polarization performance of the molybdenum electrode was evaluated in phosphoric acid solution (3.0 to 13 M). Figure 2 depicts a typical linear sweep potentiodynamic trace of the tested electrode in 3.0–13 M H3PO4. It was found that the Ecorr motivated gradually towards positive direction as the acid concentration augmented and the icorr was decreased owing to the development of different oxides of molybdenum (MoO2, MoO3, and Mo2O5) with increasing acidity. In comparison to neutral or basic media, the oxide coatings that develop on the Mo electrode are substantially highly stable in acidic ones. Also, hydrogen evolution was reduced under the same conditions. The data is given in Table 1. Following the determination of the altered molybdenum oxides' aqueous solution's thermodynamic durability, the associated equilibria could be evaluated. The passive film in acidic solutions consisted mostly of MoO2 in common with MoO3 and Mo(OH)3, which could be reduced using either Eq. (1) or Eq. (2):

Potentiodynamic polarization curves in different concentrations of H3PO4 at 298 K.

With a rise in acid concentration, an oxide layer developed on the electrode surface. The outcomes demonstrated that, in comparison to neutral and basic media, the oxide layer on Mo is somewhat highly stable in acidic medium. This behavior could be explained by the passive film's dominant element, MoO2, which comprises a negligible amount of MoO3 and Mo(OH)3. These Depending upon the solution's voltage and pH, these oxides may dissociate in aqueous solutions following the Eqs. (3, 4 and 5):

In acidic media, these equilibrium systems will tend to stabilize the solid phase. Accordingly, the barrier film will be formed. Normally, in acidic solutions, ionic molybdate species are often reactive and have the tendency to polymerize to Mo6O216−36. Therefore, the increase in acid concentration causes the large ionic species to polymerize, creating thick surface film. On the other hand, as the acid concentration rises, the rate of hydrogen evolution diminishes and also lowering the rate of corrosion.

The main corroded phosphoric concentration is 3.0 M, so the polarization curves were developed for various concentrations of NaCl in 3.0 M H3PO4 acid solution. Figure 3 depicts the potentiodynamic curve for the utilized electrode in 3.0 M H3PO4 containing NaCl of different concentrations (0.1 to 1.0 M). The corrosion voltage moves noticeably to the active path, as shown in Table 2, causing depolarization of the anodic reaction by the anion, i.e., promoting the dissolution of the investigated electrode17,37.

Potentiodynamic polarization curves of Mo in 3.0 M H3PO4 containing different concentrations of Cl− at 298 K.

Figure 4 shows the connection between the icorr and Ecorr for NaCl concentration in 3.0 M H3PO4 at 298 K. icorr value increases with the rise in Cl− amount, which proposes that Cl− ions contribute to form soluble oxochloro complexes leading to pitting nucleation at the active inclusion sites increasing the corrosion rate, or icorr. Ecorr moves to more negative values, as demonstrated in Fig. 4 and Table 2.

The variation of logicorr and Ecorr of Mo with Cl− concentrations in 3.0 M H3PO4 solution at 298 K.

By increasing anion concentration, it was observed that the hydrogen evolution and corrosion rate were greater in the acid-containing Cl−. The impact of streptomycin concentration (0.5–10 mM), as an inhibitor for the corrosion, was investigated in 3.0 M H3PO4 acid solution containing 1.0 M chloride (highly corrosive concentration or medium). The following equation was utilized to assess the inhibition efficiency (IE%) and the corrosion parameters listed in Table 338:

where icorr and iinh are the uninhibited and inhibited corrosion current densities, respectively. It can be deduced that rising streptomycin concentration in 1.0 M Cl− reduced icorr and hydrogen formation at all concentrations. Hence, the inhibitor has led to the passivation of the studied electrode through adsorption and reduction of hydrogen formation. Because the inhibitor interacts with the metal surface through lone pairs of electrons on methoxy, hydroxyl, and/or amino groups that can form oxides, which effectively protect the metal surface, this can be credited to the accumulation of the inhibitor molecules by increasing their concentration on the Mo electrode. According to H+ ion or H2O molecule reduction, respectively, the main cathodic mechanism in Mo corrosion in acidic solutions is hydrogen evolution reaction39. Due to the surface-hindering effects of both adsorption and film formation, which decrease the attack area, the increase in inhibitor concentration enhanced the corrosion inhibition efficacy to 98.85% at 10.0 mM of inhibitor. The cathodic and anodic Tafel slopes changed normally as illustrated in Fig. 5, indicating the presence of hindering effect without altering the reaction mechanism.

Potentiodynamic polarization curves of Mo in 3.0 M H3PO4 with 0.3 M Cl− solutions containing different Streptomycin concentrations at 298 K.

The Tafel behavior of the Butler-Volmer Model was estimated as follows40,41,42:

The uppermost IE (%) can be attributed to the -OCH3, NH2, OH, or C=O groups and/or π-electrons of the double bond43. Hydrogen formation is of great significance for hydrogenation reactions in the acid medium as phosphoric acid. Subsequent mechanisms may be suggested for hydrogen evolution reaction on electrodes in acidic solutions44,45:

1. a principal discharge (Volmer reaction)

2. a desorption step (Heyrowsky reaction)

3. a combination step (Tafel reaction)

First, hydronium ion is discharged46. No reaction can happen alone, however, associated with anotherVolmer response must be slow if Tafel and/or Heyrowsky reaction are both rapid. A sluggish step followed by a quick step. Hence, the inhibitor's existence may prevent MHads formation or the electron move to hydronium ion and suppress both reactions (7 & 8, respectively).

In destructive environments, the atomic hydrogen (MHads) will resyndicate, producing molecular hydrogen collected on the surface as a second step of the HER.

Figure 6 displays the EIS data for Mo electrodes in phosphoric acid of different concentrations (3.0–13 M). Bode plots demonstrated a wide maximum phase diagram, representing the existence of three-time constants47,48,49. Fitting of the spectra has been done by means of a three-time constant model in which three parallel CPEs (Q1, Q2, and Q3) were utilized (Fig. 7). The interfacial impedance (Z) is defined by50,51:

where x = 1 resembles a perfect capacitor, then the fitting information displayed that x values < 1. Thus, at ω = 1, the total reciprocal capacitance is:

Bode plots of Mo in different concentrations of H3PO4 at 298 K.

An equivalent circuit model used to fit the impedance data of Mo.

The reciprocal capacitance enlarges linearly with growing acid concentration. The simulated and the experimental outcomes indicating a well-suited model with a 3% fit error. The comparable circuit parameters are introduced in Table 4. The data indicate that RT values enlarged with growing acid concentration.

The reciprocal capacitance enlarges linearly with growing acid concentration. The simulated and the experimental outcomes indicating a well-suited model with a 3% fit error. The comparable circuit parameters are introduced in Table 4. The data indicate that RT values enlarged with growing acid concentration.

As shown in Fig. 8, the Bode plots for various NaCl concentrations in 3.0 M H3PO4 acid solution are fitted with a similar model given in Fig. 7 and the results are in Table 5. The relative thickness (1/CT) and the total resistance (RT) of the film decrease with increasing anion concentration.

Bode plots of Mo in 3.0 M H3PO4 containing different concentrations of Cl− at 298 K.

Inhibition of corrosion happens by adding the inhibitor to the highest corrosive medium (3.0 M H3PO4 containing 1.0 M chloride ion), with concentrations (0.5–10 mM) as displayed in Fig. 9. The data were best fitted with the model presented in Fig. 7 and fitted factors are provided in Table 6. Given that the passive oxide film may be compared to a dielectric plate capacitor, the equation below relates the passive film thickness (d) in cm to the capacitance (C)52,53,54:

where εo is the vacuum permittivity (0.885 × 10−11 Fcm−1), εr is the comparative dielectric constant of the film, and A is the electrode surface area in cm2. Although the genuine estimation of εr inside the film is hard to assess, a variation of C can express a difference in the film thickness. The 1/C and thickness are related directly to each other. Consequently, as the concentration of the inhibitor grows, extra inhibitor units will be accumulated on the surface via the active centers (heteroatoms or double bonds) in streptomycin, promoting an increment in film thickness and diminishing in H2 advancement.

Bode plots of Mo in 3.0 M H3PO4 with 0.3 M Cl− solutions containing different Streptomycin concentrations at 298 K.

Chloride ions can form negative charges in the interface region because of specific adsorption, and then, the streptomycin compound is protonated in the acid solution. This leads to strong adsorption of protonated drug and chloride ions, thus preventing chloride ions to attack Mo electrode surface which has positive charges in the acidic medium. The concentrations of Cl and protonated medicines are then substantially higher than those in bulk near to the interface. Due to the repulsion force between the protonated inhibitor and the positively charged surface, the protonated inhibitor medication does not directly attack the positively charged surface. It can be attached to the molybdenum surface by electrostatic contact between Cl− and protonated inhibitor. The inhibitor adsorbed on the metal through different polar groups (–OCH3, NH2, OH, or C=O) by a coordination bond. The efficiency of inhibition reaches 99.6% at 10.0 mM of inhibitor concentration which is in respectable promise with that of polarization outcomes.

The outcomes were verified by surface examination. Figure 10 signifies an example for the SEM image for the tested electrode in the air (Fig. 10a), which is a smooth sample, 3.0 M H3PO4 (Fig. 10b) is corroded surface with large pores, 13 M H3PO4 (Fig. 10c) is much more smooth surface containing some scratches, 3.0 M H3PO4 with 1.0 M NaCl (Fig. 10d) is corroded surface with precipitates of salts, 3.0 M H3PO4 with 1.0 M NaCl containing 0.5 mM streptomycin (Fig. 10e) is so smooth surface without large pores and with increasing inhibitor concentration till 10 mM streptomycin (Fig. 10f), the surface becomes more smoother.

SEM images of Mo surface (a) mechanically polished and after 2 h of immersion in (b) 3.0 M H3PO4 solution, (c) 13 M H3PO4, (d) 3.0 M H3PO4 solution comprising 1.0 M Cl−, (e) 3.0 M H3PO4 solution comprising 1.0 M Cl− and 0.5 mM Streptomycin and (f) 3.0 M H3PO4 solution comprising 1.0 M Cl− and 10 mM Streptomycin.

Gaussian quantum chemical calculations view 5.08 program is a significant matter to predict the inhibitor's molecular mechanism for adsorption on the tested alloy surface. The goal is to explore the applicability of quantum–mechanical calculations to expect the inhibition efficiency of Streptomycin. The computed quantum chemical parameters for Streptomycin are 155 alpha electrons and 154 beta electrons that can be included in the coordinate bond to be adsorbed well on the surface. This ensures its well absorbability. The Molecular volume (MV) determined as 460 cm3/mol and molecular surface area is 557 cm2. This means that the area is large enough for the inhibitor to cover the metal surface. Hence, it provides an extensively high resistance effect on surface of the metal, with noticeable inhibition efficiency growth55. The nuclear-nuclear repulsion ENN describes the electrostatic repulsion between the nuclei and is found to be 5458.69 Hartees = 148,538.5096 eV. It is also so high which confirmed the well adsorption ability of the inhibitor. Thus, its ENN, large surface molecular area and large number of alpha and beta electrons included ensure its high absorbability. Also, from calculations, ExpMin = 3.60D-02, ExpMax = 8.59D+03, ExpMxC = 1.30D+03. This means that it acts well as an electron donor compound to be adsorbed well on the alloy surface through these electrons with a coordinate bond56.

As a result of potentiodynamic polarization and EIS estimations, using surface examination and quantum chemical calculations, the following points were concluded:

The values of icorr declined with the rise of the molar concentrations of phosphoric acid.

The values of icorr increased with the rise in anion concentration and decreased with the rising in inhibitor concerntration.

Quantitative research that is based on the CPE idea provides a greater level of agreement between experimental findings and theoretical data, showing the applicability of the suggested model (two-time constants) for elucidating real-world data.

The total resistance RT values increase with rising inhibitor concentration in 3.0 M phosphoric acid containing 1.0 M NaCl at 298 K.

The datasets used and/or analyzed during the current study available from the corresponding author on reasonable request.

Hefnawy, M. A., Medany, S. S., El-Sherif, R. M. & Fadlallah, S. A. NiO-MnOx/polyaniline/graphite electrodes for urea electrocatalysis: synergetic effect between polymorphs of MnOx and NiO. ChemistrySelect 7, e202103735. https://doi.org/10.1002/slct.202103735 (2022).

Article CAS Google Scholar

Hefnawy, M. A., Medany, S. S., El-Sherif, R. M. & Fadlallah, S. A. Green synthesis of NiO/Fe3O4@chitosan composite catalyst based on graphite for urea electro-oxidation. Mater. Chem. Phys. 290, 126603. https://doi.org/10.1016/j.matchemphys.2022.126603 (2022).

Article CAS Google Scholar

Hefnawy, M. A., Medany, S. S., Fadlallah, S. A., El-Sherif, R. M. & Hassan, S. S. Novel self-assembly Pd(II)-Schiff base complex modified glassy carbon electrode for electrochemical detection of paracetamol. Electrocatalysis https://doi.org/10.1007/s12678-022-00741-7 (2022).

Article Google Scholar

Hefnawy, M. A., Fadlallah, S. A., El-Sherif, R. M. & Medany, S. S. Synergistic effect of Cu-doped NiO for enhancing urea electrooxidation: Comparative electrochemical and DFT studies. J. Alloys Compd. 896, 162857. https://doi.org/10.1016/j.jallcom.2021.162857 (2022).

Article CAS Google Scholar

Wang, H. et al. Defect-rich Ni3S4−x as a robust electrode material for supercapacitor and aqueous Ni-Zn battery applications. J. Alloys Compd. 933, 167733 (2023).

Article CAS Google Scholar

Jinlong, L., Zhuqing, W., Tongxiang, L., Ken, S. & Hideo, M. Enhancing the corrosion resistance of the 2205 duplex stainless steel bipolar plates in PEMFCs environment by surface enriched molybdenum. Results Phys. 7, 3459–3464 (2017).

Article ADS Google Scholar

Jinlong, L., Tongxiang, L. & Chen, W. Surface enriched molybdenum enhancing the corrosion resistance of 316L stainless steel. Mater. Lett. 171, 38–41 (2016).

Article Google Scholar

El-Taib Heakal, F., Ghoneim, A. A. & Fekry, A. M. Stability of spontaneous passive films on high strength Mo-containing stainless steels in aqueous solutions. J. Appl. Electrochem. 37, 405–413 (2007).

Article CAS Google Scholar

Hefnawy, M. A., Fadlallah, S. A., El-Sherif, R. M. & Medany, S. S. Competition between enzymatic and non-enzymatic electrochemical determination of cholesterol. J. Electroanal. Chem. 930, 117169. https://doi.org/10.1016/j.jelechem.2023.117169 (2023).

Article CAS Google Scholar

Zhou, T. et al. Coupling effects of tungsten and molybdenum on microstructure and stress-rupture properties of a nickel-base cast superalloy. Prog. Nat. Sci. Mater. Int. 28, 45–53 (2018).

Article CAS Google Scholar

Abbas, Q. & Binder, L. The electrochemical dissolution of molybdenum in non-aqueous media. Int. J. Refract. Met. Hard Mater. 29, 542–546 (2011).

Article CAS Google Scholar

Henderson, J. D., Li, X., Shoesmith, D. W., Noël, J. J. & Ogle, K. Molybdenum surface enrichment and release during transpassive dissolution of Ni-based alloys. Corros. Sci. 147, 32–40 (2019).

Article CAS Google Scholar

Ping, H. et al. Electrochemical corrosion behavior of titanium-zirconium-molybdenum alloy, Rare Met. Mater. Eng. 46, 1225–1230 (2017).

Google Scholar

Farahmand, R., Sohrabi, B., Ghaffarinejad, A. & Meymian, M. R. Z. Synergistic effect of molybdenum coating and SDS surfactant on corrosion inhibition of mild steel in presence of 3.5% NaCl. Corros. Sci. 136, 393–401 (2018).

Article CAS Google Scholar

Badawy, W. A. & Al-Kharafi, F. M. Corrosion and passivation behaviors of molybdenum in aqueous solutions of different pH. Electrochim. Acta. 44, 693–702 (1998).

Article CAS Google Scholar

Ameer, M. A. & Fekry, A. M. Inhibition effect of newly synthesized heterocyclic organic molecules on corrosion of steel in alkaline medium containing chloride. Int. J. Hydrogen Energy. 35, 11387–11396 (2010).

Article CAS Google Scholar

Fekry, A. M. & Ameer, M. A. Corrosion inhibition of mild steel in acidic media using newly synthesized heterocyclic organic molecules. Int. J. Hydrogen Energy. 35, 7641–7651 (2010).

Article CAS Google Scholar

Fathima, H., Pais, M. & Rao, P. The use of green inhibitors in evaluating the safe expiry dates of therapeutics. J. Bio Tribo Corros. 7, 108 (2021).

Article Google Scholar

Shukla, S. K. & Ebenso, E. E. Corrosion inhibition, adsorption behavior and thermodynamic properties of streptomycin on mild steel in hydrochloric acid medium. Int. J. Electrochem. Sci. 6, 3277–3291 (2011).

CAS Google Scholar

Sharma, T., Kumar, A., Shah, S. S. & Bamezai, R. K. Analysis of interactions between streptomycin sulphate and aqueous food acids (L-ascorbic acid and citric acid): Physico-chemical and spectroscopic insights. J. Chem. Thermodyn. 151, 106207 (2020).

Article CAS Google Scholar

Jeragh, B., Al-Wahaib, D., El-Sherif, A. A. & El-Dissouky, A. Potentiometric and thermodynamic studies of dissociation and metal complexation of 4-(3-hydroxypyridin-2-ylimino)-4-phenylbutan-2-one. J. Chem. Eng. Data. 52, 1609–1614 (2007).

Article CAS Google Scholar

Aljahdali, M., El-Sherif, A. A., Shoukry, M. M. & Mohamed, S. E. Potentiometric and thermodynamic studies of binary and ternary transition metal (II) complexes of imidazole-4-acetic acid and some bio-relevant ligands. J. Solution Chem. 42, 1028–1050 (2013).

Article CAS Google Scholar

Badawy, W. A., Ismail, K. M., Khalifa, Z. M. & Medany, S. S. Poly (2-aminobiphenyl), preparation, characterization, mechanism, and kinetics of the electropolymerization process. J. Appl. Polym. Sci. 125, 3410–3418 (2012).

Article CAS Google Scholar

Wassenaar, T. M. Use of antimicrobial agents in veterinary medicine and implications for human health. Crit. Rev. Microbiol. 31, 155–169 (2005).

Article CAS PubMed Google Scholar

Singh, B. & Mitchison, D. A. Bactericidal activity of streptomycin and isoniazid against tubercle bacilli. Br. Med. J. 1, 130 (1954).

Article CAS PubMed PubMed Central Google Scholar

Ameer, M. A. & Fekry, A. M. Corrosion inhibition of mild steel by natural product compound. Prog. Org. Coat. 71, 343–349 (2011).

Article CAS Google Scholar

Qiang, Y. et al. Experimental and theoretical studies of four allyl imidazolium-based ionic liquids as green inhibitors for copper corrosion in sulfuric acid. Corros. Sci. 119, 68–78. https://doi.org/10.1016/j.corsci.2017.02.021 (2017).

Article CAS Google Scholar

Qiang, Y., Li, H. & Lan, X. Self-assembling anchored film basing on two tetrazole derivatives for application to protect copper in sulfuric acid environment. J. Mater. Sci. Technol. 52, 63–71. https://doi.org/10.1016/j.jmst.2020.04.005 (2020).

Article CAS Google Scholar

Qiang, Y., Guo, L., Li, H. & Lan, X. Fabrication of environmentally friendly Losartan potassium film for corrosion inhibition of mild steel in HCl medium. Chem. Eng. J. 406, 126863. https://doi.org/10.1016/j.cej.2020.126863 (2021).

Article CAS Google Scholar

Qiang, Y. et al. Experimental and molecular modeling studies of multi-active tetrazole derivative bearing sulfur linker for protecting steel from corrosion. J. Mol. Liq. 351, 118638. https://doi.org/10.1016/j.molliq.2022.118638 (2022).

Article CAS Google Scholar

Wang, Y., Qiang, Y., Zhi, H., Ran, B. & Zhang, D. Evaluating the synergistic effect of maple leaves extract and iodide ions on corrosion inhibition of Q235 steel in H2SO4 solution. J. Ind. Eng. Chem. 117, 422–433. https://doi.org/10.1016/j.jiec.2022.10.030 (2023).

Article CAS Google Scholar

Hamadi, L., Mansouri, S., Oulmi, K. & Kareche, A. The use of amino acids as corrosion inhibitors for metals: A review. Egypt. J. Pet. 27, 1157–1165 (2018).

Article Google Scholar

de Araújo Macedo, R. G. M., do Nascimento Marques, N., Tonholo, J. & de Carvalho Balaban, R. Water-soluble carboxymethylchitosan used as corrosion inhibitor for carbon steel in saline medium. Carbohydr. Polym. 205, 371–376 (2019).

Article Google Scholar

Yang, G., He, P. & Qu, X.-P. Inhibition effect of glycine on molybdenum corrosion during CMP in alkaline H2O2 based abrasive free slurry. Appl. Surf. Sci. 427, 148–155 (2018).

Article ADS CAS Google Scholar

Tang, M., Dou, X., Tian, Z., Yang, M. & Zhang, Y. Enhanced hydrolysis of streptomycin from production wastewater using CaO/MgO solid base catalysts. Chem. Eng. J. 355, 586–593 (2019).

Article CAS Google Scholar

Lee, J. D. Concise Inorganic Chemistry (Chapman & Hall, Bukupedia, 1991).

Google Scholar

Hu, P. et al. Influence of concentrations of chloride ions on electrochemical corrosion behavior of titanium-zirconium-molybdenum alloy. J. Alloys Compd. 708, 367–372 (2017).

Article CAS Google Scholar

Medany, S. S., Elkamel, R. S., Abdel-Gawad, S. A. & Fekry, A. M. A novel nano-composite CSNPs/PVP/CoONPs coating for improving corrosion resistance of Ti-6Al-4V alloy as a dental implant. Metals (Basel). 12, 1784 (2022).

Article CAS Google Scholar

Heakal, F.E.-T., Fekry, A. M. & Fatayerji, M. Z. Influence of halides on the dissolution and passivation behavior of AZ91D magnesium alloy in aqueous solutions. Electrochim. Acta. 54, 1545–1557 (2009).

Article Google Scholar

Galal, A., Atta, N. F. & Hefnawy, M. A. Lanthanum nickel oxide nano-perovskite decorated carbon nanotubes/poly (aniline) composite for effective electrochemical oxidation of urea. J. Electroanal. Chem. 862, 114009 (2020).

Article CAS Google Scholar

Atta, N. F., El-Sherif, R. M. A., Hassan, H. K., Hefnawy, M. A. & Galal, A. Conducting polymer-mixed oxide composite electrocatalyst for enhanced urea oxidation. J. Electrochem. Soc. 165, J3310–J3317. https://doi.org/10.1149/2.0421815jes (2018).

Article CAS Google Scholar

Galal, A., Atta, N. F. & Hefnawy, M. A. Voltammetry study of electrocatalytic activity of lanthanum nickel perovskite nanoclusters-based composite catalyst for effective oxidation of urea in alkaline medium. Synth. Met. 266, 116372. https://doi.org/10.1016/j.synthmet.2020.116372 (2020).

Article CAS Google Scholar

Abdel-Gawad, S. A. & Fekry, A. M. A novel environmental nano-catalyst of zeolite amended with carbon nanotube/silver nanoparticles decorated carbon paste electrode for electro-oxidation of propylene glycol. Sci. Rep. 12, 1–11 (2022).

Article Google Scholar

Hefnawy, M. A., Fadlallah, S. A., El-Sherif, R. M. & Medany, S. S. Nickel-manganese double hydroxide mixed with reduced graphene oxide electrocatalyst for efficient ethylene glycol electrooxidation and hydrogen evolution reaction. Synth. Met. 282, 116959. https://doi.org/10.1016/j.synthmet.2021.116959 (2021).

Article CAS Google Scholar

Bhardwaj, M. & Balasubramaniam, R. Uncoupled non-linear equations method for determining kinetic parameters in case of hydrogen evolution reaction following Volmer–Heyrovsky–Tafel mechanism and Volmer-Heyrovsky mechanism. Int. J. Hydrogen Energy. 33, 2178–2188 (2008).

Article CAS Google Scholar

Azizi, O., Jafarian, M., Gobal, F., Heli, H. & Mahjani, M. G. The investigation of the kinetics and mechanism of hydrogen evolution reaction on tin. Int. J. Hydrogen Energy. 32, 1755–1761 (2007).

Article CAS Google Scholar

Fekry, A. & Sayed, M. Electrochemical corrosion behavior of nano-coated Ti-6Al-4V alloy by a novel chitosan nanoparticles/silver nanoparticles in artificial saliva solution. Egypt. J. Chem. 61, 747–758 (2018).

Google Scholar

Hussein, M. S. & Fekry, A. M. Effect of fumed silica/chitosan/poly (vinylpyrrolidone) composite coating on the electrochemical corrosion resistance of Ti–6Al–4V alloy in artificial saliva solution. ACS Omega 4, 73–78 (2019).

Article CAS Google Scholar

Fekry, A. M., Ghoneim, A. A. & Ameer, M. A. Electrochemical impedance spectroscopy of chitosan coated magnesium alloys in a synthetic sweat medium. Surf. Coat. Technol. 238, 126–132 (2014).

Article CAS Google Scholar

Fekry, A. M. Electrochemical behavior of a novel nano-composite coat on Ti alloy in phosphate buffer solution for biomedical applications. RSC Adv. 6, 20276–20285 (2016).

Article ADS CAS Google Scholar

Fekry, A. M. & Tammam, R. H. The influence of different anions on the corrosion resistance of Ti-6Al-4V alloy in simulated acid rainwater. Ind. Eng. Chem. Res. 53, 2911–2916 (2014).

Article CAS Google Scholar

Fekry, A. M. Impedance and hydrogen evolution studies on magnesium alloy in oxalic acid solution containing different anions. Int. J. Hydrogen Energy. 35, 12945–12951 (2010).

Article CAS Google Scholar

Fekry, A. M. The influence of chloride and sulphate ions on the corrosion behavior of Ti and Ti-6Al-4V alloy in oxalic acid. Electrochim. Acta. 54, 3480–3489 (2009).

Article CAS Google Scholar

Atta, N. F., Fekry, A. M. & Hassaneen, H. M. Corrosion inhibition, hydrogen evolution and antibacterial properties of newly synthesized organic inhibitors on 316L stainless steel alloy in acid medium. Int. J. Hydrogen Energy. 36, 6462–6471 (2011).

Article CAS Google Scholar

Dehdab, M., Yavari, Z., Darijani, M. & Bargahi, A. The inhibition of carbon-steel corrosion in seawater by streptomycin and tetracycline antibiotics: an experimental and theoretical study. Desalination 400, 7–17 (2016).

Article CAS Google Scholar

Hefnawy, M. A., Fadlallah, S. A., El-Sherif, R. M. & Medany, S. S. Systematic DFT studies of CO-Tolerance and CO oxidation on Cu-doped Ni surfaces. J. Mol. Graph. Model. 118, 108343. https://doi.org/10.1016/j.jmgm.2022.108343 (2023).

Article CAS PubMed Google Scholar

Download references

Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).

Chemistry Department, Faculty of Science, Cairo University, Giza, 12613, Egypt

Shymaa S. Medany, Yahia H. Ahmad & Amany M. Fekry

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

All authors wrote the main manuscript text and perform the experimental work. All authors reviewed the manuscript.

Correspondence to Shymaa S. Medany.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Medany, S.S., Ahmad, Y.H. & Fekry, A.M. Experimental and theoretical studies for corrosion of molybdenum electrode using streptomycin drug in phosphoric acid medium. Sci Rep 13, 4827 (2023). https://doi.org/10.1038/s41598-023-31886-0

Download citation

Received: 29 August 2022

Accepted: 20 March 2023

Published: 24 March 2023

DOI: https://doi.org/10.1038/s41598-023-31886-0

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

SHARE