Adsorption, thermodynamic, and quantum chemical investigations of an ionic liquid that inhibits corrosion of carbon steel in chloride solutions

Scientific Reports volume 12, Article number: 12536 (2022) Cite this article

1040 Accesses

8 Citations

Metrics details

An Author Correction to this article was published on 06 February 2023

An Author Correction to this article was published on 11 October 2022

This article has been updated

The purpose of this work lies in the use of ionic liquids as corrosion inhibitors due to the difficulty in some oil fields with the solubility of corrosion inhibitors and these materials can be miscible with water and thus provide a solution to such problems in the industry. The second purpose is concerned with the lower toxicity of these compounds compared with the most common corrosion inhibitors. The study covered the corrosion inhibition performance of the ionic liquid 1-butyl-3-methylimidazolium trifluoromethyl sulfonate ([BMIm]TfO) for carbon steel in 3.5% NaCl solutions. The study comprised electrochemical, adsorption, and quantum chemical investigations. The results manifested that [BMIm]TfO can be considered a promising corrosion inhibitor and the inhibition efficacy intensifies as the concentration rises. The observed inhibitive effect can be correlated to the adsorption of the ionic liquid species and the creation of protecting films on the surface. The mode of adsorption follows the Langmuir adsorption isotherm. The polarization results showed that the ionic liquid [BMIm]TfO functions as a mixed inhibitor. Reliance of the corrosion influence on the temperature in the existence and absence of [BMIm]TfO was demonstrated in the temperature range of 303–333 K using polarization data. Activation parameters were determined and discussed. The observed inhibition performance of [BMIm]TfO was correlated with the electronic properties of the ionic liquid using a quantum chemical study.

Corrosion is a serious and extremely costly problem especially in petrochemicals and petroleum production operations1,2. Besides the high potential to employ more advanced corrosion-resistant components, carbon steel tills are the main fabricated material used for the huge pipeline's construction in the different crude oil processing stages such as extraction, transmission, and storage Carbon steel pipes have been widely employed in transporting gases and liquids3,4. One of the most aggressive surroundings in petroleum production and oil refining processes is the saline water environment which contains different amounts of dissolved salts, especially sodium chloride5,6. The protective oxide film created on the surface can deteriorate in the existence of chloride ions based on an aggressive environment7,8.

Different corrosion mitigation regimes can be applied to reduce the harmful corrosion impacts. Among the conventional corrosion mitigation techniques, the utilization of eco-friendly inhibitors has advantages such as, e.g., high feasibility, high efficiency, and minimization the environmental hazards9. In recent times, ionic liquids were proven to be effective, eco-friendly inhibitors for the corrosion of different types of metals and alloys in corrosive environments such as basic, acidic, or salty solutions10,11. Due to their bulky structure and the presence of heteroatoms, ionic liquids are regarded as potential corrosion inhibitors12.

Ionic liquids, in general, have a promising corrosion inhibition tendency due to their capacity for the adsorptive contact with the surface, which forms protective layers against corrosive media. In general, the majority of ionic liquids exhibit this tendency. The types of cations and anions present in ionic liquids have a direct bearing on the levels of adsorption and inhibition efficiency that may be achieved with those liquids. In a recent study, we demonstrated that the ionic liquid 1-butyl-1-methylpyrrolidinium trifluoromethyl sulfonate ([BMP]TfO) may serve as a bi-functional inhibitor for both the corrosion of carbon steel in chloride solutions and the growth of bacteria. [BMP]TfO inhibits both types of corrosion13. It was also shown that the ionic liquids 1-(2-hydroxyethyl)-3-methylimidazolinium chloride and 1-ethyl-3-methyleimidazolinium chloride are effective corrosion inhibitors and biocides. These findings were published in the journal Ionic Liquids14. It was shown that the integration of the hydroxy group in the imidazolium cation enhances the corrosion inhibition impact15. In this paper, the corrosion inhibition performance of the ionic liquid [BMIm]TfOfor carbon steel in 3.5% NaCl solutions was demonstrated. The study comprised electrochemical, adsorption, and quantum chemical investigations.

High purity [BMIm]TfO, was obtained from Io.Li.Tec.Co., Germany, and it was used as received. Carbon steel specimens having dimensions of (5.6 cm L, 2.7 cm W, and 0.5 cm T) were used for the standard procedures of the corrosion measurements. Before use, the steel coupons were abraded with proper emery papers to give a homogeneous surface. An aggressive solution of 3.5% NaCl was prepared as a simulated corrosive environment. Different concentrations of the employed ionic liquid, 25, 50, 100, 200, and 500 ppm, were used, and various temperatures of 303, 313, 323, and 333 K, were applied.

For the electrochemical measurements, a common cell, fitted with a reference electrode—saturated calomel reference electrode (SCE) a counter electrode (CE), platinum, and the working electrode (WE), carbon, steel, was utilized. All electrochemical tests were performed employing a Volta lab 40 Potentiostat PGZ 301. Polarization experiments were carried out by sweeping the electrode potential at a rate of 2 mVs−1 and recordings the current. All polarization data were fitted using the fitting tools implemented in Volta Master 4 software by Tafel extrapolation method. The frequency range of 100 kHz–0.05 Hz with an amplitude peak of 10 mV using an AC signal was applied for the electrochemical impedance measurements. The impedance curves were fitted using the ZSimpWin3.60 software. For weight loss measurements, rectangular-shaped steel specimens with dimensions of 3 cm × 5 cm × 0.05 cm were used. The immersion time was 6 h in 3.5% NaCl at different temperatures in the absence and presence of different concentrations of [BMIm]TfO.

A scanning electron microscope, JEOL model JSM-53000, was employed for investigating the morphology of the electrodes. The quantum chemical investigations were executed using MP2 functional with a 3–21 G (d,p) basis set. The energies of high occupied molecular orbital (EHOMO) and low unoccupied molecular orbital (ELUMO) were estimated. Furthermore, the energy gap between LUMO and HOMO (ΔE) was determined16.

The curves of Fig. 1 show potentiodynamic polarization responses of carbon steel in 3.5% NaCl solutions free and containing different amounts of [BMIm]TfO. The parameters obtained from the polarization curves, corrosion currents and potentials (icorr, Ecorr, respectively), corrosion rate (CR), inhibition efficiency based on corrosion current density (EFicorr%), and efficiency based on the corrosion rate (EFCR %), cathodic Tafel slope (bc), and anodic Tafel slope (ba) are presented in Table 1. As shown in Fig. 1, the polarization curve recorded in absence of [BMIm]TfO exhibits an active trend as the current steeply rises with sweeping the potential. In addition to the ionic liquid inhibitor, a slight impact was noticed on the cathodic branch of the curve. However, a pronounced effect was recorded on the anodic branch. Both the cathodic and anodic curves shift to more negative and more positive potentials, respectively, on the addition of the [BMIm]TfO revealing the inhibiting influence.

Potentiodynamic polarization curves for the carbon steel in a 3.5% NaCl medium with and without different concentrations of [BMIm]TfO.

As the content of [BMIm]TfO increases, the current density decreases, and subsequently the corrosion rate reduces Table 1. The highest inhibition efficiency was 75% for the inhibitor concentration of 800 ppm. The observed inhibition influence is due to the creation of a protecting layer because of the adsorption of the ionic liquid species on the electrode surface. This layer isolates the surface from the corrosive environment which, in turn, leads to the observed inhibition. The extent of covering the surface (Ɵ) [BMIm]TfO was estimated. The degree of surface coverage rises as the content of [BMIm]TfO in the electrolyte increases. Full coverage of the electrode surface by the ionic liquid species was not reached in the studied concentration range of [BMIm]TfO.

The dependence of the corrosion inhibiting efficacy of [BMIm]TfO on the concentration and temperature was explored. Figure 2a manifests the change in the inhibiting efficiency with the concentration of [BMIm]TfO at various temperatures. As seen, the inhibiting efficacy rises as the [BMIm]TfO concentration increases for all temperatures. Figure 2b displays the dependence of the inhibition efficiency on the temperature of the electrolyte at different concentrations of [BMIm]TfO. It is seen that at one, and the same concentration of [BMIm]TfO, the corrosion inhibition efficacy decreases as the temperature increases. At higher concentrations of [BMIm]TfO, the extent of the negative influence of the temperature on the inhibition efficiency shrinks17.

The dependence of the inhibition efficiency of [BMIm]TfO on the corrosion of carbon steel in 3.5% NaCl solutions as a function of (a) temperature and (b) concentration.

The corrosion inhibition performance of [BMIm]TfO was investigated using the electrochemical impedance spectroscopy (EIS) technique. Figure 3 exhibits the Nyquist plots of the carbon steel electrode in the test electrolyte-free and containing different concentrations of [BMIm]TfO. As manifested in Fig. 3, the plots show imperfect capacitive loops. The higher the loop diameter always reveals stop corrosion resistance18. With the addition of [BMIm]TfO, the diameter increases signifying its inhibiting effect on the corrosion of carbon steel in the test electrolyte. This is attributable to the adsorption and formation of a protecting film of the ionic liquid on the electrode surface. This film masks the surface, leading to the lessening of the corrosion attack as evidenced by the reduction of the estimated double layer capacitance Cdl, Table 2. Also, the values of (RS), (RP1), and (RP2) increase as the content of [BMIm]TfO increases19.

Typical Nyquist plots for the carbon steel in 3.5% NaCl without and with different concentrations of [BMIm]TfO.

The equivalent circuit used to fit the Nyquist plots is shown in Fig. 4. The values of the estimated EIS parameters are compiled in Table 2. The parameters include the solution resistance (Rs), the constant phase element (Q), the polarization resistance between the surface and the formed film during the immersion in the test electrolyte (Rp1), the capacitance of double layer (Cdl), and the corrosion resistance at the surface film/electrolyte interface (Rp2).

Equivalent circuit model fitted the electrochemical impedance spectroscopy (EIS) data.

Adsorption isotherm studies were performed to explore the nature of the interaction of the ionic liquid species with the carbon steel surface. Several adsorption isotherms can describe the relationship between the extent of surface coverage and the content of adsorbed species such as Langmuir, Freundlich, and Temkin isotherms. The adsorptive interaction of [BMIm]TfO was found to obey Langmuir isotherm. The Langmuir adsorption isotherm can be defined in the following Eq. (1)20.

where (θ) is the surface coverage degree (obtained previously from EIS and PDP measurements), (Cinb) is the concentration of [BMIm]TfO, and (Kads) is the adsorption equilibrium constant.

Plotting the Langmuir relation between Cinb/θ and Cinb gives significant straight lines with a correlation coefficient of unity and an average slope value of 1.35, Fig. 5a. Thus, it is evidence that the ionic liquid species are adsorbed in absence of any side interactions18. The equilibrium constant for [BMIm]TfO adsorption (Kads) was calculated using the intercept of the Cinb/θ versus Cinb line, Table 3. Consequently, Kads value was employed to estimate the adsorption standard free energy (ΔG°ads) based on the Eq. (2):

Langmuir (a) and Temkin (b) isotherms for adsorption of the ionic liquid on the carbon steel in 3.5% NaCl solutions.

where R, T, and 55.5 are gas constant, the temperature of the system, and water molecules concentration in molar. The values of ∆Goads were determined for the ionic liquid inhibitor at different temperatures as shown in Table 3. It is seen that the high negative values of ∆Goads are correlated to the impulsive adsorption performance of [BMIm]TfOon the surface and refer to the steadiness state of the adsorbed layer. This behaviour indicates the intensive interaction between the ionic liquid constituents and the electrode surface21. As a common concept, the values of ∆Goads up to − 20 kJ mol−1 are associated with the electrostatic interaction of the charged compounds with the charged surface in which the adsorption process, in this case, is only physical. With increasing the values of ∆Goads above − 40 kJ mol−1 the chemical adsorption will be found22.

From the obtained measurements, the values of ∆Goads were stabilized at − 31 kJ mol−1 in the temperature range from 303 to 333 K. This indicates that the adsorption of ionic liquid species is typical physical sorption. The results reveal that the adsorption of the species of the ionic liquid, typically the imidazolium cation, occurs physically, electrostatically, via the interaction between the imidazolium cation and the charged centers on the electrode surface. The spontaneous nature of the adsorption of the ionic liquid species on the surface is indicated by the negative values of ∆Goads23. The heat of adsorption ∆Hoads was also estimated from the Van't Hoff Eq. (3):

By plotting the relation between ln Kads against 1/T a straight line is obtained as manifested in Fig. 5b. The slope of the obtained line is equivalent to (− ∆Hoads/R) in which the adsorption heat value (∆Hoads) is nearly the standard adsorption heat value under the testing procedures20. From the thermodynamics, the standard entropy of adsorption (∆Soads) can be obtained using the Eq. (4):

The calculated thermodynamic parameters (∆Goads, ∆Hoads and ∆Soads) are compiled in Table 3. It is seen that the ∆Hoads value is negative (− 73 KJ mol−1) indicating the impact of [BMIm]TfO adsorption on the surface. By inspection of the values of (∆Soads) as listed in Table 3, it is obvious that the ∆Soads value is the negative sign (− 162 J mol−1 K−1). The negative signal of ∆Soads can be correlated to dissolute medium which is generally proved as a growth in the disorder, as the reactants are turning into efficient complexes. Moreover, the observed manner can be explained by the substitution mechanism of more water molecules throughout the adsorption process of ionic liquid on the surface24.

Additional to the thermodynamic investigations, the kinetic activation model is also an important technique to study the inhibition mechanism and explain the features of the protective action of [BMIm]TfO at different temperatures. Arrhenius equation was employed to estimate the activation parameters of the corrosion see Eq. (5)25:

where, (CR) represents the corrosion rate, (Ea) is the energy of activation, (R) is the gas constant, and (A) is the pre-exponential factor.

The Arrhenius plots of the relation between the ln (CR) and 1/T are depicted in Fig. 6a. As seen, a linear behavior is obtained and the slopes of the straight lines is (− Ea/R) hence, the values of the activation energy (Ea) in the presence and absence of various concentrations of [BMIm]TfO were determined. Moreover, there is another formulation for the transition state as described in the following Eq. (6)26.

(a) Arrhenius and (b) Transition-state plots for carbon steel corrosion in 3.5% NaCl without and with different concentrations of [BMIm]TfO.

The terms of the equation are, Plank's constant (h), Avogadro's number (N), the activation entropy (∆S*), and the activation enthalpy (∆H*). The plots of ln CR/T versus 1/T for the ionic liquid inhibitor are presented in Fig. 6b. The slope of the obtained lines equals (−∆ H*/R) and the intercept is (lnR/Nh + ∆S*/R), hence the values of ∆H* and ∆S*can be estimated. At definite concentration ranges of the ionic liquid inhibitor, the activation parameters for carbon steel in sodium chloride medium are gathered and illustrated in Table 4. The results reveal that with the existence of [BMIm]TfO the activation energy rises, and the activation enthalpy slightly reduces meanwhile the values of the entropy for the corrosion process significantly rise. The energy of activation (Ea), which is the minimal amount of energy required to launch a chemical reaction, reaches a value of 24 kJ mol−1 at a high ionic liquid content and for the blank solution is only 16 kJ mol−1. The increase of the Ea value under the effect of ionic liquid inhibitor might be attributed to the physical sorption regime27. Additional explanation reported that the raising of the activation energy value might also be attributable to the gradual reduction in the adsorption process of [BMIm]TfO on the surface under the effect of heat. Based on these phenomena, as the adsorption process reduces more desorption action of ionic liquid species occurs as the protection and dissolution systems are in balance. It is also revealed that the sequential values of Ea and ∆Ho as presented in Table 4 are varied in the same trend confirming the common thermodynamic phenomena. On particular monitoring, it has been observed that the value of the activation entropies is negative signifying that the activated complex is in the rate-determining stage and demonstrating combination rather than separation28.

The utilization of surface analytical techniques is quite significant for realizing the characteristics of materials, especially the metallic surfaces after exposure to the various aggressive environments. SEM–EDX examination of the electrode surface following dipping in the test electrolytes was performed. The SEM images of Fig. 7a and b show the surface after the exposure to3.5% NaCl without and with the addition of [BMIm]TfO, respectively. Figure 7a representative the SEM image of the uninhibited steel surface shows a deteriorated, rough surface as a result of the corrosion29.

SEM images of (a) polished carbon steel, and (b) after 24 h of immersion in 3.5% NaCl and [BMIm]TfO.

In the absence of [BMIm]TfO the whole surface of the carbon steel is usually concealed with the corrosion products. The porous corrosion product layer is unable to protect the surface from extreme corrosion. The addition of the ionic liquid inhibitor to the test electrolyte reduced the aggressive attack on the steel surface as revealed in Fig. 7b. The surface is relatively free from the corrosion products and compared with the uninhibited sample the surface is smoother signifying the inhibiting action of [BMIm]TfO30.

Figure 8 represents the EDX spectrum of the uninhibited sample Fig. 8a and inhibited sample Fig. 8b since it shows confirms the SEM results as, in addition to the Fe, O, and C peaks, a peak of N is recorded owing to the adsorption of the imidazolium cation leading to the observed corrosion inhibition. Furthermore, under the continuation of the IL coverage, the spectrum intensities decrease because of the formation of the IL adsorptive layer on the surface31.

EDX spectra of (a) polished carbon steel, (b) after 24 h of immersion in 3.5% NaCl and [BMIm]TfO.

As known, the application of quantum chemical calculations is necessary to demonstrate the relation between the molecular/electronic structure of the inhibitor and its corrosion inhibiting efficiency32. Furthermore, the theoretical studies allow the optimum pre-selection of the inhibitor with the desired characteristics33.

The molecular geometry of the employed ionic liquid was optimized using the PM6 semiempirical method. The optimized structures were then re-optimized by ab initio Hartree–Fock method (HF) using 6–31 + G(d,p) basis set at Hartree–Fock level (HF)34, and by density functional theory (DFT) method using 6–31 + G(d,p) basis set. The values of the calculated bond length, bond angle, and dihedral angle using the DFT 6–31 + G (d,p) method are compiled in Table 5. All calculations were made by gaussian 09 W software using the B3LYP functional35. B3LYPutilizesBache's three-parameter functional (B3) and comprises a combination of HF with DFT exchange terms and the Lee, Yang, and Parr (LYP) correlation functional36.

The optimized molecular structure, the electrostatic potential feature, and the identical HOMO and LUMO electron density surfaces of the ionic liquid inhibitor, as demonstrated patterns by IL employing PM3 model chemistry, are symbolized in Fig. 9a–d. From the optimized structure, Fig. 9a it is seen the planar pentagon structure of the imidazolium ring. The electrostatic potential Fig. 9b it shows the electron cloud around the chemical structure. The sequential distribution of electrons of HOMO Fig. 9c shows information about the positions or locations that are significant in the system to accord the electrons to the contrasting orbital of the recipient molecule. On the other hand, the prevalence of electrons of LUMO Fig. 9d shows information about the molecule sites that are restricted to recognize the electron from a-convenient granter one37.

The frontier molecular orbital (a) optimized structure, (b) electrostatic potential (ESP), (c) HOMO, and (d) LUMO of the ionic liquid [BMIm]TfO.

From Fig. 9c, it is obvious that the electron density of the HOMO is generally combined with the imidazolium cation in the ionic liquid structure indicating the contribution of the imidazolium ring in the adsorption of ionic liquid on the steel surface. This is consistent with the recently published results which indicated, based on quantum chemical studies, that the imidazolium ring is likely the crucial active site in imidazolium-based ionic liquids38. The calculated values of the quantum chemical parameters, EHOMO, ELUMO, and ΔE, which are mainly affected by the electron interactions between the steel surface and the ionic liquid inhibitor were illustrated in Table 6. The EHOMO value describes the ability of the inhibitor to donate electrons to the electrode surface, while the ELUMO measures the capability to receive electrons into the LUMO molecule from a suited donor molecule39,40,41. The energy gap (ΔE), which is obtained from the difference between ELUMO and EHOMO, is also a substantial factor that can be employed to detect the molecule's activity. Mainly, the minimal ΔE value is related to large inhibition efficiency and chemical reactivity42,43,44. This means the inhibitor on the surface more easily gives/receives electrons and subsequently the adsorption of the inhibitor on the surface becomes easier. The negative sign of EHOMO refers to the physical adsorption nature of the ionic liquid inhibitor45,46,47.

In the light of the above results, it can be concluded that the employed ionic liquid is electrostatically adsorbed on the steel surface and the imidazolium cation is responsible for the observed inhibiting influence as the imidazolium ring is parallelly absorbed on the steel surface.

[BMIm]TfO was examined as a possible corrosion inhibitor for carbon steel in chloride solutions. The results revealed the inhibiting action of [BMIm]TfO which increases as the concentration increases. The potentiodynamic polarization results showed that the ionic liquid is a mixed inhibitor as both cathodic and anodic processes were influenced. The inhibiting act of [BMIm]TfO is attributable to the adsorption of the imidazolium cations on the carbon steel surface establishing a barrier layer that protects the surface from the aggressive medium. The adsorption of the [BMIm]TfO was found to obey Langmuir isotherm. The free energy of adsorption revealed that the adsorption of the ionic liquid species occurs physically via the electrostatic interaction of the imidazolium cation with the charged centers on the electrode surface. The results proved that ionic liquids can be used as corrosion inhibitors for carbon steel in brine solutions with a high efficiency that enables them to compete with the commercial inhibitors currently used, despite their high price, they are considered competitive for more than one reason, including their effectiveness and the most important reason is that they are less toxic and therefore in line with the global trend to replace toxic materials. So, it could be currently used with potential effects and less toxic materials, which makes these materials ready to compete in the field of oil and gas industry.

The datasets generated and/or analyzed during the current study are available in this published article.

The original online version of this Article was revised: In the original version of this Article, A. M. El Shamy and S. Zein El Abedin were incorrectly affiliated with ‘Petrochemicals Department, Egyptian Petroleum Research Institute, P.B. 11727, Nasr City, Cairo, Egypt.’ The correct affiliation is: ‘Electrochemistry and Corrosion Laboratory, Physical Chemistry Department, National Research Centre, Dokki, 12622, Cairo, Egypt.’

The original online version of this Article was revised: The original version of this Article contained errors in the Affiliations. Full informationregarding the corrections made can be found in the correction for this Article.

A Correction to this paper has been published: https://doi.org/10.1038/s41598-022-22010-9

A Correction to this paper has been published: https://doi.org/10.1038/s41598-023-28979-1

Sun, C., Liu, J., Sun, J., Lin, X. & Wang, Y. Probing the initial corrosion behavior of X65 steel in CCUS-EOR environments with impure supercritical CO2 fluids. Corros. Sci. 1, 109585 (2021).

Article Google Scholar

Reda, Y., Yehia, H. M. & El-Shamy, A. M. Microstructural and mechanical properties of Al-Zn alloy 7075 during RRA and triple aging. Egypt. J. Pet. 31, 9–13. https://doi.org/10.1016/j.ejpe.2021.12.001 (2022).

Article Google Scholar

Zohdy, K. M., El-Sherif, R. M. & El-Shamy, A. M. Corrosion and passivation behaviors of tin in aqueous solutions of different pH. J. Bio- Tribo-Corros. 7(2), 1–7. https://doi.org/10.1007/s40735-021-00515-6 (2021).

Article Google Scholar

Sarkar, T. K., Saraswat, V., Mitra, R. K., Obot, I. B. & Yadav, M. Mitigation of corrosion in petroleum oil well/tubing steel using pyrimidines as efficient corrosion inhibitor: Experimental and theoretical investigation. Mater. Today Commun. 26, 101862 (2021).

Article CAS Google Scholar

Azam, M. A., Sukarti, S. & Zaimi, M. Corrosion behavior of API-5L-X42 petroleum/natural gas pipeline steel in South China Sea and Strait of Melaka seawaters. Eng. Fail. Anal. 115, 104654 (2020).

Article CAS Google Scholar

Abdel-Karim, A. M., El-Shamy, A. M. & Reda, Y. Corrosion and stress corrosion resistance of Al Zn alloy 7075 by nano-polymeric coatings. J. Bio- Tribo Corros. 8, 57. https://doi.org/10.1007/s40735-022-00656-2 (2022).

Article Google Scholar

Zhang, S. et al. A study on the interaction between chloride ions and CO2 towards carbon steel corrosion. Corros. Sci. 167, 108531 (2020).

Article CAS Google Scholar

Abbas, M. A. & Bedair, M. A. Adsorption and computational studies for evaluating the behavior of silicon based compounds as novel corrosion inhibitors of carbon steel surfaces in acidic media. Z. Phys. Chem. 233, 225–254 (2019).

Article CAS Google Scholar

Tan, B. et al. Insight into the anti-corrosion performance of two food flavors as eco-friendly and ultra-high-performance inhibitors for copper in sulfuric acid medium. J. Colloid Interface Sci. 609, 838–851. https://doi.org/10.1016/j.jcis.2021.11.085 (2022).

Article CAS PubMed Google Scholar

Tan, B. et al. Passiflora edulia Sims leaves extract as renewable and degradable inhibitor for copper in sulfuric acid solution. Colloids Surf. A 645, 128892. https://doi.org/10.1016/j.colsurfa.2022.128892 (2022).

Article CAS Google Scholar

El-Shamy, A. M., El-Hadek, M. A., Nassef, A. E. & El-Bindary, R. A. Optimization of the influencing variables on the corrosion property of steel alloy 4130 in 3.5 wt.% NaCl solution. J. Chem. 2020, 9212491. https://doi.org/10.1155/2020/9212491 (2020).

Article CAS Google Scholar

El-Shamy, A. M., El-Hadek, M. A., Nassef, A. E. & El-Bindary, R. A. Box-Behnken design to enhance the corrosion resistance of high strength steel alloy in 3.5 wt.% NaCl solution. Mor. J. Chem. 8(4), 788–800. https://doi.org/10.48317/IMIST.PRSM/morjchem-v8i4.21594 (2020).

Article CAS Google Scholar

Attia, H., Mohamed Nawal, H., Soad, M. & Samar, M. Phytochemical and pharmacological studies on Convolvulus fatmensis Ktze. J. Nat. Remed. 7(1), 109–119 (2007).

Google Scholar

Bhaskaran, Y. et al. To evaluate an ionic liquid for anticorrosive impact on iron–carbon steel: Synthesis, computational and experimental mechanism. Chem. Pap. 75, 789–803 (2021).

Article CAS Google Scholar

Mohsenifar, F., Jafari, H. & Sayin, K. Investigation of thermodynamic parameters for steel corrosion in acidic solution in the presence of N, N′-Bis (phloroacetophenone)-1, 2 propanediamine. J. Bio- Tribo- Corros. 2, 1 (2016).

Article Google Scholar

Reda, Y., El-Shamy, A. M. & Eessaa, A. K. Effect of hydrogen embrittlement on the microstructures of electroplated steel alloy 4130. Ain Shams Eng. J. 9(4), 2973–2982. https://doi.org/10.1016/j.asej.2018.08.004 (2018).

Article Google Scholar

Gad, E. A. & El-Shamy, A. M. Mechanism of corrosion and microbial corrosion of 1,3-dibutyl thiourea using the quantum chemical calculations. J. Bio- Tribo- Corros. 8, 71. https://doi.org/10.1007/s40735-022-00669-x (2022).

Article Google Scholar

Xu, X., Singh, A., Sun, Z., Ansari, K. R. & Lin, Y. Theoretical, thermodynamic and electrochemical analysis of biotin drug as an impending corrosion inhibitor for mild steel in 15% hydrochloric acid. R. Soc. Open Sci. 4, 170933 (2017).

Article PubMed PubMed Central Google Scholar

Hossain, N., Asaduzzaman Chowdhury, M. & Kchaou, M. An overview of green corrosion inhibitors for sustainable and environment friendly industrial development. J. Adhes. Sci. Technol. 35, 673–690 (2021).

Article CAS Google Scholar

Ardakani, E. K., Kowsari, E., Ehsani, A. & Ramakrishna, S. Performance of all Ionic Liquids as the eco-friendly and sustainable compounds in inhibiting corrosion in various media: A comprehensive review. Microchem. J. 165, 106049 (2021).

Article CAS Google Scholar

El-Shamy, A. M., Zakaria, K., Abbas, M. A. & El Abedin, S. Z. Anti-bacterial and anti-corrosion effects of the ionic liquid 1-butyl-1-methylpyrrolidinium trifluoromethylsulfonate. J. Mol. Liq. 211, 363–369 (2015).

Article CAS Google Scholar

Mouneir, S. M., El-Hagrassi, A. M. & El-Shamy, A. M. A review on the chemical compositions of natural products and their role in setting current trends and future goals. Egypt. J. Chem. 65(5), 491–506. https://doi.org/10.21608/ejchem.2021.95577.4486 (2022).

Article Google Scholar

Sherif, E. S. M., Abdo, H. S. & El Abedin, S. Z. Corrosion inhibition of cast iron in Arabian gulf seawater by two different ionic liquids. Materials 8, 3883–3895 (2015).

Article CAS PubMed PubMed Central Google Scholar

Shehata, M. F., El-Shamy, A. M., Zohdy, K. M., Sherif, E. S. M. & Zein El Abedin, S. Studies on the antibacterial influence of two ionic liquids and their corrosion inhibition performance. Appl. Sci. 10, 1444 (2020).

Article CAS Google Scholar

Musa, A. Y., Mohamad, A. B., Kadhum, A. A. H., Takriff, M. S. & Ahmoda, W. Quantum chemical studies on corrosion inhibition for series of thio compounds on mild steel in hydrochloric acid. J. Ind. Eng. Chem. 18, 551–555 (2012).

Article CAS Google Scholar

Abdel-Karim, A. M. & El-Shamy, A. M. A review on green corrosion inhibitors for protection of archeological metal artifacts. J. Bio- Tribo- Corros. 8, 35. https://doi.org/10.1007/s40735-022-00636-6 (2022).

Article Google Scholar

Kabel, K. I., Zakaria, K., Abbas, M. A. & Khamis, E. A. Assessment of corrosion inhibitive behavior of 2-aminothiophenol derivatives on carbon steel in 1 M HCl. J. Ind. Eng. Chem. 23, 57–66 (2015).

Article CAS Google Scholar

Joshi, S. J., Deshmukh, A. & Sarma, H. Biotechnology for Sustainable Environment (Springer, 2021).

Book Google Scholar

Verma, C. et al. Aryl sulfonamidomethylphosphonates as new class of green corrosion inhibitors for mild steel in 1 M HCl: Electrochemical, surface and quantum chemical investigation. J. Mol. Liq. 209, 306–319 (2015).

Article CAS Google Scholar

Bakr, A. A., Zakaria, K., Abbas, M. A. & Hamdy, A. Amphistegina media filtration as pretreatment of SWRO desalination unit for producing different salinities to study the corrosion behavior of various materials. Desalin. Water Treat. 57, 16703–16720 (2016).

CAS Google Scholar

Ouakki, M. et al. Electrochemical, thermodynamic and theoretical studies of some imidazole derivatives compounds as acid corrosion inhibitors for mild steel. J. Mol. Liq. 319, 114063 (2020).

Article CAS Google Scholar

Soliman, S. A., Metwally, M. S., Selim, S. R., Bedair, M. A. & Abbas, M. A. Corrosion inhibition and adsorption behavior of new Schiff base surfactant on steel in acidic environment: Experimental and theoretical studies. J. Ind. Eng. Chem. 20, 4311–4320 (2014).

Article CAS Google Scholar

Farag, A. A., Ismail, A. S. & Migahed, M. A. Environmental-friendly shrimp waste protein corrosion inhibitor for carbon steel in 1 M HCl solution. Egypt. J. Pet. 27, 1187–1194 (2018).

Article Google Scholar

Mashuga, M. E. et al. Adsorption, thermodynamic and quantum chemical studies of 1-hexyl-3-methylimidazolium based ionic liquids as corrosion inhibitors for mild steel in HCl. Materials 8, 3607–3632 (2015).

Article CAS PubMed Central Google Scholar

Abbass, M., Mohammed, K. Z. & Hamdy, A. Adsorption properties and inhibitive effect of antibacterial drug on carbon steel corrosion in HCl medium. Biosci. Biotechnol. Res. Asia. 9, 27–37 (2012).

Article CAS Google Scholar

Hameed, R. S. A., Ismail, E. A., Al-Shafey, H. I. & Abbas, M. A. Expired indomethacin therapeutics as corrosion inhibitors for carbon steel in 1.0 M hydrochloric acid media. J. Bio- Tribo-Corros. 6, 1–10 (2020).

Google Scholar

Gece, G. The use of quantum chemical methods in corrosion inhibitor studies. Corros. Sci. 50, 2981–2992 (2008).

Article CAS Google Scholar

Frisch, M. et al. Gaussian 09, Revision A. 01 (2009).

Lee, C., Yang, W. & Parr, R. G. Development of the Colle-Salvetti correlation-energy formula into a functional of the electron density. Phys. Rev. B. 37, 785 (1988).

Article CAS Google Scholar

Tian, G. & Yuan, K. Adsorption and inhibition behavior of imidazolium tetrafluoroborate derivatives as green corrosion inhibitors for carbon steel. J. Mol. Model. 27, 1–16 (2021).

Article Google Scholar

Singh, A. K. et al. Evaluation of anti-corrosion performance of an expired semi-synthetic antibiotic cefdinir for mild steel in 1 M HCl medium: An experimental and theoretical study. Results Phys. 14, 102383 (2019).

Article Google Scholar

Zohdy, K. M., El-Sherif, R. M., Ramkumar, S. & El-Shamy, A. M. Quantum and electrochemical studies of the hydrogen evolution findings in corrosion reactions of mild steel in acidic medium. Upstream Oil Gas Technol. 6, 100025. https://doi.org/10.1016/j.upstre.2020.100025 (2021).

Article Google Scholar

Karthikaiselvi, R. & Subhashini, S. Study of adsorption properties and inhibition of mild steel corrosion in hydrochloric acid media by water-soluble composite poly (vinyl alcohol-o-methoxy aniline). J. Assoc. Arab Univ. Basic Appl. Sci. 16, 74–82 (2014).

Google Scholar

Tang, Y. et al. A preliminary investigation of corrosion inhibition of mild steel in 0.5 M H2SO4 by 2-amino-5-(n-pyridyl)-1, 3, 4-thiadiazole: Polarization, EIS and molecular dynamics simulations. Corros. Sci. 52, 1801–1808 (2010).

Article CAS Google Scholar

Farag, H. K., El-Shamy, A. M., Sherif, E. M. & El Abedin, S. Z. Sonochemical synthesis of nanostructured ZnO/Ag composites in an ionic liquid. Z. Phys. Chem. 230(12), 1733–1744. https://doi.org/10.1515/zpch-2016-0777 (2016).

Article CAS Google Scholar

Abbas, M. A., Zakaria, K., El-Shamy, A. M. & El Abedin, S. Z. Utilization of 1-butylpyrrolidinium chloride ionic liquid as an eco-friendly corrosion inhibitor and biocide for oilfield equipment: Combined weight loss, electrochemical and SEM studies Z. Phys. Chem. 235(4), 377–406. https://doi.org/10.1515/zpch-2019-1517 (2019).

Article CAS Google Scholar

El-Shamy, A. M. & Abdel Bar, M. M. Ionic liquid as water soluble and potential inhibitor for corrosion and microbial corrosion for iron artifacts. Egypt. J. Chem. 64(4), 1867–1876. https://doi.org/10.21608/ejchem.2021.43786.2887 (2021).

Article Google Scholar

Download references

Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB). This work was supported by own.

Petroleum Applications Department, Egyptian Petroleum Research Institute, P.B. 11727, Nasr City, Cairo, Egypt

Mohamed A. Abbas

Petrochemicals Department, Egyptian Petroleum Research Institute, P.B. 11727, Nasr City, Cairo, Egypt

Amr S. Ismail

Analysis and Evaluation Department, Egyptian Petroleum Research Institute, P.B. 11727, Nasr City, Cairo, Egypt

K. Zakaria

Electrochemistry and Corrosion Laboratory, Physical Chemistry Department, National Research Centre, Dokki, 12622, Cairo, Egypt

A. M. El-Shamy & S. Zein El Abedin

You can also search for this author in PubMed Google Scholar

M.A.A., A.S.I., and K.Z. analyzed the data and wrote the experimental work in this manuscript; S.Z.E.A. act as a consultant for the scientific information, and S.Z.E.A. and A.M.E.-S. helped perform the analysis with constructive discussions.

Correspondence to A. M. El-Shamy.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Abbas, M.A., Ismail, A.S., Zakaria, K. et al. Adsorption, thermodynamic, and quantum chemical investigations of an ionic liquid that inhibits corrosion of carbon steel in chloride solutions. Sci Rep 12, 12536 (2022). https://doi.org/10.1038/s41598-022-16755-6

Download citation

Received: 27 April 2022

Accepted: 14 July 2022

Published: 22 July 2022

DOI: https://doi.org/10.1038/s41598-022-16755-6

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Journal of Bio- and Tribo-Corrosion (2023)

Chemical Papers (2023)

Journal of Bio- and Tribo-Corrosion (2023)

Scientific Reports (2022)

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Blog

Adsorption, thermodynamic, and quantum chemical investigations of an ionic liquid that inhibits corrosion of carbon steel in chloride solutions